Compound for organic electronic element, organic electronic element using same, and electronic device thereof

ABSTRACT

Provided are an organic electronic element and an electronic device thereof, comprising a mixture of a compound of Formula 1 as a phosphorescent host material and thereby achieving high light-emitting efficiency, low driving voltage and improved lifespan.

BACKGROUND Technical Field

The present invention relates to compound for organic electronic element, organic electronic element using the same, and an electronic device thereof.

Background Art

In general, organic light emitting phenomenon refers to a phenomenon that converts electronic energy into light energy by using an organic material. An organic electronic element using an organic light emitting phenomenon usually has a structure including an anode, a cathode, and an organic material layer interposed therebetween. Here, in order to increase the efficiency and stability of the organic electronic element, the organic material layer is often composed of a multi-layered structure composed of different materials, and for example, may include a hole injection layer, a hole transport layer, an emitting layer, an electron transport layer, an electron injection layer and the like.

A material used as an organic material layer in an organic electronic element may be classified into a light emitting material and a charge transport material, such as a hole injection material, a hole transport material, an electron transport material, an electron injection material and the like depending on its function.

In the case of a polycyclic compound containing a heteroatom, the difference in properties according to the material structure is so large that it is applied to various layers as a material of an organic electronic element. In particular, it has characteristics of different band gaps (HOMO, LUMO), electronical characteristics, chemical properties, and physical properties depending on the number of rings, fused positions and the type and arrangement of heteroatoms, therefore application development for layers of various organic electronic elements using the same has been progressed.

As a representative example thereof, in the following Patent Documents 1 to 4, the performance of the 5-membered cyclic compound in the polycyclic compound has been reported depending on the hetero type, arrangement, substituent type, fused position, and the like.

[Patent Document 1]: U.S. Pat. No. 5,843,607

[Patent Document 2]: Japanese Laid-Open Patent Publication No. 1999-162650

[Patent Document 3]: Korean Published Patent Application No. 2008-0085000

[Patent Document 4]: US Patent Publication No. 2010-0187977

[Patent Document 5]: Korean Published Patent Application No. 2011-0018340

[Patent Document 6]: Korean Published Patent 2009-0057711

Patent Documents 1 and 2 disclose an embodiment in which the indolocarbazole core in which the hetero atom in the 5-membered cyclic compound is composed only of nitrogen (N) is used, and an aryl group substituted or unsubstituted in N of indolocarbazole is used. However, in the prior invention 1, there exists only a simple aryl group substituted or unsubstituted with an alkyl group, an amino group, an alkoxy group, or the like as a substituent, so that the effect of the substituents of the polycyclic compounds was very poor to prove, and only the use as a hole transport material is described, and the use thereof as a phosphorescent host material is not described.

Patent Documents 3 and 4 disclose a compound in which pyridine, pyrimidine, triazine or the like containing an aryl group and N is substituted for an indolocarbazole core having a hetero atom N in the same 5-membered cyclic compound as in the above Patent Documents 1 and 2, however only the use examples for phosphorescent green host materials are described, and the performance for other heterocyclic compounds substituted for indolocarbazole core is not described.

In Patent Documents 5, Nitrogen (N), oxygen (O), sulfur (S), carbon and the like are described as heteroatom in the 5-membered cyclic compound, however there are only examples using the same heteroatom in the performance measurement data, the performance characteristics of a 5-membered cyclic compound containing a different heteroatom could not be confirmed.

Therefore, the patent document does not disclose solutions to low charge carrier mobility and low oxidation stability of a 5-membered cyclic compound containing same heteroatom.

When the 5-membered cyclic compound molecules are generally laminated, as the adjacent π-electrons increase, they have a strong electronical interaction, and this is closely related to the charge carrier mobility, particularly, the same 5-membered cyclic compound of N—N type has an edge-to-face morphology as an order of arrangement of molecules when molecules are laminated, otherwise a different 5-membered cyclic compound with different heteroatoms has an antiparallel cofacial π-stacking structure in which the packing structure of the molecules is opposite to each other, so that the arrangement order of the molecules becomes face-to-face morphology. It is reported that the steric effect of the substituent substituted on the asymmetrically arranged hetero atom N as the cause of this laminated structure causes relatively high carrier mobility and high oxidation stability (Org. Lett. 2008, 10, 1199).

In Patent Document 6, an example of using as a fluorescent host material for various polycyclic compounds having seven or more membered cyclic compounds has been reported.

As described above, the fused positions, the number of rings, the arrangement of heteroatoms, and characteristic change by type of the polycyclic compounds have not yet been sufficiently developed.

Particularly, in a phosphorescent organic electronic element using a phosphorescent dopant material, the LUMO and HOMO levels of the host material have a great influence on the efficiency and life span of the organic electronic element, this is because the charge balance control in the emitting layer, the quenching of the dopant, and the reduction in efficiency and life span due to light emission at the interface of the hole transport layer can be prevented, depending on whether electron and hole injection in the emitting layer can be efficiently controlled.

For fluorescent and phosphorescent host materials, recently we have been studying the increase of efficiency and life span of organic electronic elements using TADF (thermal activated delayed fluorescent), exciplex, etc., particularly, and many studies have been carried out to identify the energy transfer method from the host material to the dopant material.

Although there are various methods for identifying the energy transfer in the emitting layer for TADF (thermally activated delayed fluorescent) and exciplex, it can be easily confirmed by the PL lifetime (TRTP) measurement method.

The TRTP (Time Resolved Transient PL) measurement method is a method of observing a decay time over time after irradiating the host thin film with a pulsed light source, and therefore it is possible to identify the energy transfer method by observing the energy transfer and the lag time. The TRTP measurement can distinguish between fluorescence and phosphorescence, an energy transfer method in a mixed host material, an exciplex energy transfer method, and a TADF energy transfer method.

There are various factors affecting the efficiency and life span depending on the manner in which the energy is transferred from the host material to the dopant material, and the energy transfer method differs depending on the material, so that the development of stable and efficient host material for organic electronic element has not yet been sufficiently developed. Therefore, development of new materials is continuously required, and especially development of a host material for an emitting layer is urgently required.

DETAILED DESCRIPTION OF THE INVENTION Summary

The present invention has been proposed in order to solve the problems of the phosphorescent host material, and an object of the present invention is, by controlling the HOMO level of a host material of a phosphorescent emitting organic electronic element including a phosphorescent dopant, to provide a compound capable of controlling charge balance and of improving efficiency and life span in an emitting layer, and an organic electronic element using the same and an electronic device thereof.

Technical Solution

In order to control the efficient hole injection and electron injection in the emitting layer of the phosphorescence emitting organic electronic element, by introducing a seven-ring heterocyclic core of the host material and a specific substituent effect, the charge balance in the emitting layer is maximized, thereby providing a low driving voltage, high efficiency, and high life of the organic electronic device.

The present invention provides an organic electronic element comprising a first electrode, a second electrode, and an organic material layer formed between the first electrode and the second electrode, wherein the organic material layer includes an emitting layer, and the emitting layer includes a first host compound represented by the following Formula (20) and a second host compound represented by the following Formula (1) as phosphorescence emitting layer, and in addition, includes a compound represented by any of following Formula (1) and (20).

The present invention also provides an organic electronic element using the compound represented by the above formula and an electronic device thereof.

Effects of the Invention

By using the mixture according to the present invention as a phosphorescent host material, it is possible to achieve a high luminous efficiency and a low driving voltage of an organic electric element, and the life span of the device can be greatly improved.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an illustration of an organic electroluminescent device according to the present invention.

FIG. 2 shows the HOD result according to the embodiment of the present invention.

FIG. 3 shows the EOD result according to the embodiment of the present invention.

-   100: organic electric element, -   110: substrate -   120: the first electrode(anode), -   130: the hole injection layer -   140: the hole transport layer, -   141: a buffer layer -   150: the emitting layer, -   151: the emitting auxiliary layer -   160: the electron transport layer, -   170: the electron injection layer -   180: the second electrode(cathode)

DETAILED DESCRIPTION

Hereinafter, some embodiments of the present invention will be described in detail. Further, in the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.

In addition, terms, such as first, second, A, B, (a), (b) or the like may be used herein when describing components of the present invention. Each of these terminologies is not used to define an essence, order or sequence of a corresponding component but used merely to distinguish the corresponding component from other component(s). It should be noted that if a component is described as being “connected”, “coupled”, or “connected” to another component, the component may be directly connected or connected to the other component, but another component may be “connected”, “coupled” or “connected” between each component.

As used in the specification and the accompanying claims, unless otherwise stated, the following is the meaning of the term as follows.

Unless otherwise stated, the term “halo” or “halogen”, as used herein, includes fluorine, bromine, chlorine, or iodine.

Unless otherwise stated, the term “alkyl” or “alkyl group”, as used herein, has a single bond of 1 to 60 carbon atoms, and means saturated aliphatic functional radicals including a linear alkyl group, a branched chain alkyl group, a cycloalkyl group (alicyclic), an cycloalkyl group substituted with a alkyl or an alkyl group substituted with a cycloalkyl.

Unless otherwise stated, the term “haloalkyl” or “halogen alkyl”, as used herein, includes an alkyl group substituted with a halogen.

Unless otherwise stated, the term “heteroalkyl”, as used herein, means alkyl substituted one or more of carbon atoms consisting of an alkyl with hetero atom.

Unless otherwise stated, the term “alkenyl” or “alkynyl”, as used herein, has double or triple bonds of 2 to 60 carbon atoms, but is not limited thereto, and includes a linear or a branched chain group.

Unless otherwise stated, the term “cycloalkyl”, as used herein, means alkyl forming a ring having 3 to 60 carbon atoms, but is not limited thereto.

Unless otherwise stated, the term “alkoxyl group”, “alkoxy group” or “alkyloxy group”, as used herein, means an oxygen radical attached to an alkyl group, but is not limited thereto, and has 1 to 60 carbon atoms.

Unless otherwise stated, the term “alkenoxyl group”, “alkenoxy group”, “alkenyloxyl group” or “alkenyloxy group”, as used herein, means an oxygen radical attached to an alkenyl group, but is not limited thereto, and has 2 to 60 carbon atoms.

Unless otherwise stated, the term “aryloxyl group” or “aryloxy group”, as used herein, means an oxygen radical attached to an aryl group, but is not limited thereto, and has 6 to 60 carbon atoms.

Unless otherwise stated, the term “aryl group” or “arylene group”, as used herein, has 6 to 60 carbon atoms, but is not limited thereto. Herein, the aryl group or arylene group means a monocyclic and polycyclic aromatic group, and may also be formed in conjunction with an adjacent group. Examples of “aryl group” may include a phenyl group, a biphenyl group, a fluorene group, or a spirofluorene group.

The prefix “aryl” or “ar” means a radical substituted with an aryl group. For example, an arylalkyl may be an alkyl substituted with an aryl, and an arylalenyl may be an alkenyl substituted with aryl, and a radical substituted with an aryl has a number of carbon atoms as defined herein.

Also, when prefixes are named subsequently, it means that substituents are listed in the order described first. For example, an arylalkoxy means an alkoxy substituted with an aryl, an alkoxylcarbonyl means a carbonyl substituted with an alkoxyl, and an arylcarbonylalkenyl also means an alkenyl substituted with an arylcarbonyl, wherein the arylcarbonyl may be a carbonyl substituted with an aryl.

Unless otherwise stated, the term “heteroalkyl”, as used herein, means alkyl containing one or more of hetero atoms. Unless otherwise stated, the term “heteroaryl group” or “heteroarylene group”, as used herein, means a C2 to C60 aryl containing one or more of hetero atoms or arylene group, but is not limited thereto, and includes at least one of monocyclic and polycyclic rings, and may also be formed in conjunction with an adjacent group.

Unless otherwise stated, the term “heterocyclic group”, as used herein, contains one or more heteroatoms, but is not limited thereto, has 2 to 60 carbon atoms, includes any one of monocyclic and polycyclic rings, and may include heteroaliphadic ring and/or heteroaromatic ring. Also, the heterocyclic group may also be formed in conjunction with an adjacent group.

Unless otherwise stated, the term “heteroatom”, as used herein, represents at least one of N, O, S, P, or Si.

Also, the term “heterocyclic group” may include a ring containing SO₂ instead of carbon consisting of cycle. For example, “heterocyclic group” includes compound below.

Unless otherwise stated, the term “aliphatic”, as used herein, means an aliphatic hydrocarbon having 1 to 60 carbon atoms, and the term “aliphatic ring”, as used herein, means an aliphatic hydrocarbon ring having 3 to 60 carbon atoms.

Unless otherwise stated, the term “ring”, as used herein, means an aliphatic ring having 3 to 60 carbon atoms, or an aromatic ring having 6 to 60 carbon atoms, or a hetero ring having 2 to 60 carbon atoms, or a fused ring formed by the combination of them, and includes a saturated or unsaturated ring.

Other hetero compounds or hetero radicals other than the above-mentioned hetero compounds include, but are not limited thereto, one or more heteroatoms.

Unless otherwise stated, the term “carbonyl”, as used herein, is represented by —COR′, wherein R′ may be hydrogen, an alkyl having 1 to 20 carbon atoms, an aryl having 6 to 30 carbon atoms, a cycloalkyl having 3 to 30 carbon atoms, an alkenyl having 2 to 20 carbon atoms, an alkynyl having 2 to 20 carbon atoms, or the combination of these.

Unless otherwise stated, the term “ether”, as used herein, is represented by —R—O—R′, wherein R or R′ may be independently hydrogen, an alkyl having 1 to 20 carbon atoms, an aryl having 6 to 30 carbon atoms, a cycloalkyl having 3 to 30 carbon atoms, an alkenyl having 2 to 20 carbon atoms, an alkynyl having 2 to 20 carbon atoms, or the combination of these.

Unless otherwise stated, the term “substituted or unsubstituted”, as used herein, means that substitution is substituted by at least one substituent selected from the group consisting of, but is not limited thereto, deuterium, halogen, an amino group, a nitrile group, a nitro group, a C₁-C₂₀ alkyl group, a C₁-C₂₀ alkoxyl group, a C₁-C₂₀ alkylamine group, a C₁-C₂₀ alkylthiopen group, a C₆-C₂₀ arylthiopen group, a C₂-C₂₀ alkenyl group, a C₂-C₂₀ alkynyl group, a C₃-C₂₀ cycloalkyl group, a C₆-C₂₀ aryl group, a C₆-C₂₀ aryl group substituted by deuterium, a C₈-C₂₀ arylalkenyl group, a silane group, a boron group, a germanium group, and a C₂-C₂₀ heterocyclic group.

Unless otherwise expressly stated, Formula used in the present invention, as used herein, is applied in the same manner as the substituent definition according to the definition of the exponent of the following Formula.

Wherein, when a is an integer of zero, the substituent R¹ is absent, when a is an integer of 1, the sole substituent R¹ is linked to any one of the carbon constituting the benzene ring, when a is an integer of 2 or 3, they are respectively combined as follows, in which R¹ may be the same or different from each other, and when a is an integer of 4 to 6, and it combines to the carbon of the benzene ring in a similar manner, whereas the indication of hydrogen combines to the carbon forming the benzene ring is omitted.

Unless otherwise expressly stated, the terms “ortho”, “meta”, and “para” used in the present invention refer to the substitution positions of all substituents, and the ortho position indicates the position of the substituent immediately adjacent to the compound, for example, when benzene is used, it means 1 or 2 position, and the meta position is the next substitution position of the neighbor substitution position, when benzene as an example stands for 1 or 3 position, and the para position is the next substitution position of the meta position, which means 1 and 4 position when benzene is taken as an example. A more detailed example of the substitution position is as follows, and it can be confirmed that the ortho-, and meta-position are substituted by non-linear type and para-positions are substituted by linear type.

[Example of Ortho-Position]

[Example of Meta-Position]

[Example of Para-Position]

Hereinafter, a compound according to an aspect of the present invention and an organic electric element comprising the same will be described.

The present invention provides a compound represented by the following Formula (1)

{In Formula 1,

1) Ar⁴ is selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b))(where, L′ is selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic, and the R_(a) and R_(b) are independently selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic group containing at least one hetero atom of O, N, S, Si, or P), 2) c is an of 0 to 6, and d and e are integer of 0 to 4, 3) R³, R⁴ and R⁵ are the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); or in case c, d and e are 2 or more, and R³, R⁴ and R⁵ are each in plural being the same or different, and a plurality of R³ or a plurality of R⁴ or a plurality of R⁵ may combine each other to form a ring. 4) L² is independently selected from the group consisting of a single bond, a C₆-C₆₀ arylene group, and a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic group, 5) X¹ is O or S, wherein, aryl group, fluorenyl group, arylene group, heterocyclic group, fused ring group, alkyl group, alkenyl group, alkoxy group and aryloxy group may be substituted with one or more substituents selected from the group consisting of deuterium; halogen; a silane group substituted or unsubstituted with C₁-C₂₀ alkyl group or C₆-C₂₀ aryl group; siloxane group; boron group; germanium group; cyano group; nitro group; -L′-N(R_(a))(R_(b)); a C₁-C₂₀ alkylthio group; C₁-C₂₀ alkoxyl group; C₁-C₂₀ alkyl group; C₂-C₂₀ alkenyl group; C₂-C₂₀ alkynyl group; C₆-C₂₀ aryl group; C₆-C₂₀ aryl group substituted with deuterium; a fluorenyl group; C₂-C₂₀ heterocyclic group; C₃-C₂₀ cycloalkyl group; C₇-C₂₀ arylalkyl group and C₈-C₂₀ arylalkenyl group, and also, these substituents may combine each other and form a ring, wherein the term ‘ring’ means C₃-C₆₀ aliphatic ring or C₆-C₆₀ aromatic ring or a C₂-C₆₀ heterocyclic ring or a fused ring formed by the combination of them, and includes a saturated or unsaturated ring.}

Formula (1) comprises a compound represented by the following Formula (2)

{In Formula (2),

1) wherein R³, R⁴, R⁵, L², c, d, e and X¹ are the same as defined above,

2) Z¹, Z², and Z³ are each independently selected from the group consisting of CR⁰ or N, and R⁰ is each independently selected from the group consisting of hydrogen; deuterium; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); 3) z is an integer of 0 to 2, 4) R¹¹ is the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); or When R¹¹ and R⁰ of Z combine or when z is 2, adjacent R¹¹s may combine to each other to form an aromatic or heteroaromatic ring.}

The compound represented by Formula (1) provides a compound represented by any of the following Formula (3) to (7).

{In Formula (3) to (7),

1) wherein R³, R⁴, R⁵, L², c, d, e and X¹ are the same as defined above,

2) z is an integer of 0 to 2,

3) R¹¹ is the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); or the z is combined with a plurality or neighboring substituents R⁰ to form an aromatic or heteroaromatic ring.}

The present invention includes a compound represented by any one of the following Formula (8) to (19) when R¹¹ in Formula (1) forms a ring.

{In Formula (8) to (19),

1) R³, R⁴, R⁵, L², c, d, e and X¹ are the same as defined above,

2) Z¹, Z², and Z³ are each independently selected from the group consisting of CR⁰ or N, and R⁰ is each independently selected from the group consisting of hydrogen; deuterium; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); 3) Ar⁵ and Ar⁶ are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)), 4) Y¹ and Y² are each independently NR′, O, S or CR′R″, and R′ and R″ are each independently hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₃-C₆₀ heterocyclic group; a C₁-C₅₀ alkyl group; and R′ and R″ may combine with each other to form a ring with a spiro.}

The present invention provides an organic electronic element comprising a first electrode, a second electrode, and an organic material layer formed between the first electrode and the second electrode, wherein the organic material layer includes an emitting layer, and the emitting layer comprises a first host compound represented by Formula (20) and a second host compound represented by Formula (1) as the phosphorescent light emitting layer

{In Formula (20) and (1),

1) Ar¹, Ar², Ar³, and Ar⁴ are each independently selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b))(where, L′ is selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic, and the R_(a) and R_(b) are independently selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic group containing at least one hetero atom of O, N, S, Si, or P), and also Ar² and Ar³ may combine each other to form a ring, 2) a is an of 0 to 4, and b is an integer of 0 to 3, and c is an integer of 0 to 6, and d is an integer of 0 to 4, and e is an integer of 0 to 4. 3) R¹, R², R³, R⁴ and R⁵ are the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); or in case a, b, c, and e are 2 or more, and d is 2, and R¹, R², R³, R⁴ and R⁵ are each in plural being the same or different, and a plurality of R¹ or a plurality of R² or a plurality of R³ or a plurality of R⁴ or a plurality of R⁵ may combine to each other to form a ring. 4) L¹ and L² are independently selected from the group consisting of a single bond, a C₆-C₆₀ arylene group, and a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic group, 6) X¹ is O or S, 7) n is an integer of 1 or 2, and when n is 2, there are two Ar² and two Ar³, wherein two Ar² are the same or different, and two Ar³ are the same or different, wherein, aryl group, fluorenyl group, arylene group, heterocyclic group, fused ring group, alkyl group, alkenyl group, alkoxy group and aryloxy group may be substituted with one or more substituents selected from the group consisting of deuterium; halogen; a silane group substituted or unsubstituted with C₁-C₂₀ alkyl group or C₆-C₂₀ aryl group; siloxane group; boron group; germanium group; cyano group; nitro group; -L′-N(R_(a))(R_(b)); a C₁-C₂₀ alkylthio group; C₁-C₂₀ alkoxyl group; C₁-C₂₀ alkyl group; C₂-C₂₀ alkenyl group; C₂-C₂₀ alkynyl group; C₆-C₂₀ aryl group; C₆-C₂₀ aryl group substituted with deuterium; a fluorenyl group; C₂-C₂₀ heterocyclic group; C₃-C₂₀ cycloalkyl group; C₇-C₂₀ arylalkyl group and C₈-C₂₀ arylalkenyl group, and also, these substituents may combine each other and form a ring, wherein the term ‘ring’ means C₃-C₆₀ aliphatic ring or C₆-C₆₀ aromatic ring or a C₂-C₆₀ heterocyclic ring or a fused ring formed by the combination of them, and includes a saturated or unsaturated ring.}

In a specific aspect of the invention, the compound represented by Formula (20) includes a compound represented by the following Formula (21) or Formula (22)

{In Formula (21) and Formula (22), R¹, R², L¹, Ar¹, Ar², Ar³, a and b are the same as defined above.}

The present invention provides an organic electric element comprising a compound, wherein L¹ and L² in Formulas (1) and (20) are selected from any one of the group consisting of the following formulas (A-1) to (A-12)

{In Formula (A-1) to (A-12),

1) a′, c′, d′ and e′ are integer of 0 to 4; and b′ is an integer of 0 to 6; and f′ and g′ are integer of 0 to 3, and h′ is an integer of 0 to 1,

2) R⁶, R⁷ and R⁸ are the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); Or when f′ and g′ are 2 or more, R⁶, R⁷ and R⁸ are the same or different from each other, and plurality of R⁶ or plurality of R⁷ or plurality of R⁸ may combine each other to form an aromatic or a heteroaromatic ring, two adjacent R⁶ and R⁷, or R⁷ and R⁸ may combine to form an aromatic or heteroaromatic ring, 3) Y is NR′, O, S or CR′R″, and R′ and R″ are each independently hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₃-C₆₀ heterocyclic group; a C₁-C₅₀ alkyl group; and R′ and R″ may combine to each other to form a ring with a spiro. 4) Z⁴, Z⁵ and Z⁶ are independently of each other CR′ or N and at least one is N.}

The compound represented by Formula (20) is represented by any of the following Formulas (23) to (26)

{In Formulas (23) to (26),

1) R¹, R², L¹, Ar¹, Ar², Ar³, a and b are the same as defined above, and

2) R⁶, R⁷, c′, d′, f′, g′ and Y are the same as defined above.}

The compound represented by Formula (20) is represented by any one of the following Formulas (27) to (38)

{In Formulas (27) to (38),

R¹, R², L¹, Ar¹, Ar², Ar³, a and b are the same as defined above.}

The compound represented by Formula (20) is represented by the following Formula (39) or Formula (40).

{In Formulas (39) to (40),

R¹, R², L¹, Ar¹, Ar², Ar³, a and b are the same as defined above.}

The compound represented by Formula (20) is represented by the following Formula (41).

{In Formula (41),

1) R¹, R², L¹, Ar¹, Ar², Ar³, a and b are the same as defined above,

2) f is an integer of 0 to 3, and g is an integer of 0 to 4,

3) R⁹ and R¹⁰ are the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); or in case f and g are 2 or more, each as plurality are the same as or different from each other, and a plurality of R⁹ or a plurality of R¹⁰ or adjacent R⁹ and R¹⁰ may combine to each other to form an aromatic or a heteroaromatic ring, 4) Y is NR′, O, S or CR′R″, 5) R′ and R″ are each independently hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₃-C₆₀ heterocyclic group; a C₁-C₅₀ alkyl group; and R′ and R″ may combine to each other to form a ring with a spiro.}

The compound represented by Formula (1) is represented by the following Formulas 3-1 to 3-92 and Formulas 4-1 to 4-92:

The compound represented by Formula (20) is represented by the following Formulas 1-1 to 1-68 and Formulas 2-1 to 2-68:

Referring to FIG. 1, the organic electric element (100) according to the present invention includes a first electrode (120) formed on a substrate (110), a second electrode (180), and an organic material layer including the compound represented by Formula 1 between the first electrode (120) and the second electrode (180). Here, the first electrode (120) may be an anode (positive electrode), and the second electrode (180) may be a cathode (negative electrode). In the case of an inverted organic electric element, the first electrode may be a cathode, and the second electrode may be an anode.

The organic material layer may include a hole injection layer (130), a hole transport layer (140), an emitting layer (150), an electron transport layer (160), and an electron injection layer (170) formed in sequence on the first electrode (120). Here, the remaining layers except the emitting layer (150) may not be formed. The organic material layer may further include a hole blocking layer, an electron blocking layer, an emitting-auxiliary layer (151), an electron transport auxiliary layer, a buffer layer (141), etc., and the electron transport layer (160) and the like may serve as a hole blocking layer.

Although not shown, the organic electric element according to the present invention may further include a protective layer formed on at least one side of the first and second electrodes, which is a side opposite to the organic material layer.

Otherwise, even if the same core is used, the band gap, the electrical characteristics, the interface characteristics, and the like may vary depending on which substituent combines at which position, therefore the choice of core and the combination of sub-substituents associated therewith is also very important, and in particular, when the optimal combination of energy levels and T1 values and unique properties of materials (mobility, interfacial characteristics, etc.) of each organic material layer is achieved, a long life span and high efficiency can be achieved at the same time.

The organic electroluminescent device according to an embodiment of the present invention may be manufactured using a PVD (physical vapor deposition) method. For example, a metal or a metal oxide having conductivity or an alloy thereof is deposited on a substrate to form a cathode, and the organic material layer including the hole injection layer (130), the hole transport layer (140), the emitting layer (150), the electron transport layer (160), and the electron injection layer (170) is formed thereon, and then depositing a material usable as a cathode thereon can manufacture an organic electroluminescent device according to an embodiment of the present invention.

In addition, an emitting auxiliary layer (151) may be further formed between the hole transport layer (140) and the emitting layer (150), and an electron transport auxiliary layer may be further formed between the emitting layer (150) and the electron transport layer (160).

In addition, at least one hole transporting band layer is provided between the first electrode and the emitting layer, and the hole transporting band layer may include a hole transport layer, an emitting auxiliary layer, or both, and the hole transporting band layer may provide an organic electronic element comprising the compound represented by Formula (20)

The present invention may further include a light efficiency enhancing layer formed on at least one of the opposite side to the organic material layer among one side of the first electrode, or one of the opposite side to the organic material layer among one side of the second electrode.

Also, the present invention provides the organic electric element wherein the organic material layer is formed by one of a spin coating process, a nozzle printing process, an inkjet printing process, a slot coating process, a dip coating process or a roll-to-roll process, and since the organic material layer according to the present invention can be formed by various methods, the scope of the present invention is not limited by the method of forming the organic material layer.

As another specific example, the present invention provides an organic electric element wherein the emitting layer in the organic material layer is a phosphorescent light emitting layer.

The compound represented by Formula (1) is used as a phosphorescent light emitting layer and is a red phosphorescent host

The compounds represented by Formula (1) and by Formula (20) are mixed in a ratio of any one of 1:9 to 9:1 to be included in the emitting layer of the organic material layer.

The compound represented by Formula (1) and by Formula (20) are mixed in a ratio of any one of 1:9 to 5:5 to be included in the emitting layer of the organic material layer.

The organic electric element according to an embodiment of the present invention may be a front emission type, a back emission type, or a both-sided emission type, depending on the material used.

WOLED (White Organic Light Emitting Device) has advantages of high resolution realization and excellent fairness, and can be manufactured using conventional LCD color filter technology. Various structures for a white organic light emitting device mainly used as a backlight device have been proposed and patented. Representatively, there are side-by-side arrangement of the radiation part of the red (R), green (G) and blue (B), a stacking method in which R, G, and B emitting layers are laminated on top and bottom, electroluminescence by the blue (B) organic emitting layer and, by using the light from this, a color conversion material (CCM) method using a photo-luminescence of an inorganic phosphor, etc., and the present invention may be applied to such WOLED.

The present invention also provides an electronic device comprising a display device comprising the organic electric element; and a control part driving the display device.

According to another aspect, the present invention provides a display device wherein the organic electric element is at least one of an OLED, an organic solar cell, an organic photo conductor, an organic transistor(organic TFT) and an element for monochromic or white illumination. Here, the electronic device may be a wired/wireless communication terminal which is currently used or will be used in the future, and covers all kinds of electronic devices including a mobile communication terminal such as a cellular phone, a personal digital assistant(PDA), an electronic dictionary, a point-to-multipoint(PMP), a remote controller, a navigation unit, a game player, various kinds of TVs, and various kinds of computers.

Hereinafter, Synthesis Examples of the compound represented by Formulas (1) and (20) of the present invention and preparation examples of the organic electric element of the present invention will be described in detail by way of example, but are not limited to the following examples.

Synthesis Example 1

The final products 1 represented by Formula (20) according to the present invention can be synthesized by reaction between Sub 1 and Sub 2 as illustrated in the following Reaction Scheme 1.

In Reaction Scheme 1, n is 1 each, and when n is 2, the detailed reaction schemes are as shown in the following Reaction Schemes 1-1 and 1-2.

Synthesis Examples of Sub 1

When L¹ in Sub 1 of Reaction Scheme 1 is not a single bond, it can be synthesized by the reaction path of the following Reaction Scheme 2, but is not limited thereto.

Synthesis Examples of Sub 1-3(1)

3-bromo-9-phenyl-9H-carbazole (45.1 g, 140 mmol) was dissolved in DMF 980 mL, Bispinacolborate (39.1 g, 154 mmol), PdCl₂(dppf)catalyst (3.43 g, 4.2 mmol), KOAc (41.3 g, 420 mmol) were added in order and stirred for 24 hours and then after synthesizing the borate compound, the obtained compound was separated over a silicagel column and recrystallization to give 35.2 g of the borate compound (yield: 68%).

Synthesis Examples of Sub 1-3(2)

2-bromo-9-phenyl-9H-carbazole (76.78 g, 238.3 mmol), Bis(pinacolato)diboron (66.57 g, 262.1 mmol), Pd(dppf)Cl₂ (5.84 g, 7.1 mmol), KOAc (70.16 g, 714.9 mmol) were carried out in the same manner as in Sub 1-3 (1) to obtain 73.92 g (yield: 84%) of the product Sub 1-3 (2).

Synthesis Examples of Sub 1(10)

9-phenyl-3-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole (29.5 g, 80 mmol) were dissolved in THF 360 mL, 3-bromo-3′-iodo-1,1′-biphenyl (30.16 g, 84 mmol), Pd(PPh₃)₄(2.8 g, 2.4 mmol), NaOH (9.6 g, 240 mmol), 180 mL of water were added and were refluxed with stirring. After the reaction was completed, the reaction mixture was extracted with ether and water. The organic layer was dried over MgSO₄ and concentrated. The resulting organic material was separated by silicagel column chromatography and recrystallization to obtain 26.56 g (yield: 70%) of the product.

Synthesis Examples of Sub 1(3)

9-phenyl-2-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole (29.5 g, 80 mmol), THE 360 mL, 1-bromo-4-iodobenzene (23.8 g, 84 mmol), Pd(PPh₃)₄(2.8 g, 2.4 mmol), NaOH (9.6 g, 240 mmol), and 180 mL of water were carried out in the same manner as in Sub 1(10) to obtain 22.9 g of the product Sub 1(3) (yield: 72%).

Synthesis Examples of Sub 1(5)

9-phenyl-2-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole (73.92 g, 200.2 mmol) were dissolved in THE 880 mL in a round bottom flask, 1-bromo-2-iodobenzene (85.0 g, 300.3 mmol), Pd(PPh₃)₄(11.6 g, 10 mmol), K₂CO₃ (83 g, 600.6 mmol), and 440 mL of water were carried out in the same manner as in Sub 1(10) to obtain 55.8 g of the product Sub 1(5) (yield: 70%).

Synthesis Examples of Sub 1(15)

9-phenyl-2-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole (73.92 g, 200.2 mmol) were dissolved in THF 880 mL in a round bottom flask, 2-bromo-7-iododibenzo[b,d]furan (112.0 g, 300.3 mmol), Pd(PPh₃)₄(11.6 g, 10 mmol), K₂CO₃ (83 g, 600.6 mmol), and 440 mL of water were carried out in the same manner as in Sub 1(10) to obtain 72.4 g of the product Sub 1(15) (yield: 74%).

Synthesis Examples of Sub 1(22)

9-phenyl-2-(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9H-carbazole (73.92 g, 200.2 mmol) were dissolved in THE 880 mL in a round bottom flask, 1,3-dibromo-5-iodobenzene (108.65 g, 300.3 mmol), Pd(PPh₃)₄(11.6 g, 10 mmol), K₂CO₃(83 g, 600.6 mmol), and 440 mL of water were carried out in the same manner as in Sub 1(10) to obtain 69.7 g of the product Sub 1(22) (yield: 73%).

Examples of Sub 1 are as follows, but are not limited thereto.

TABLE 1 compound FD-MS compound FD-MS Sub 1(1) m/z = 321.02(C₁₈H₁₂BrN = 322.21) Sub 1(2) m/z = 321.02(C₁₈H₁₂BrN = 322.21) Sub 1(3) m/z = 397.05(C₂₄H₁₆BrN = 398.30) Sub 1(4) m/z = 563.12(C₃₇H₂₆BrN = 564.53) Sub 1(5) m/z = 397.05(C₂₄H₁₆BrN = 398.30) Sub 1(6) m/z = 397.05(C₂₄H₁₆BrN = 398.30) Sub 1(7) m/z = 473.08(C₃₀H₂₀BrN = 474.40) Sub 1(8) m/z = 473.08(C₃₀H₂₀BrN = 474.40) Sub 1(9) m/z = 473.08(C₃₀H₂₀BrN = 474.40) Sub 1(10) m/z = 473.08(C₃₀H₂₀BrN = 474.40) Sub 1(11) m/z = 473.08(C₃₀H₂₀BrN = 474.40) Sub 1(12) m/z = 473.08(C₃₀H₂₀BrN = 474.40) Sub 1(13) m/z = 497.08(C₃₂H₂₀BrN = 498.42) Sub 1(14) m/z = 503.03(C₃₀H₁₈BrNS = 504.45) Sub 1(15) m/z = 487.06(C₃₀H₁₈BrNO = 488.38) Sub 1(16) m/z = 513.11(C₃₃H₂₄BrN = 514.47) Sub 1(17) m/z = 473.08(C₃₀H₂₀BrN = 474.40) Sub 1(18) m/z = 628.13(C₃₉H₂₅BrN₄ = 629.56) Sub 1(19) m/z = 589.14(C₃₉H₂₈BrN = 590.56) Sub 1(20) m/z = 627.13(C₄₀H₂₆BrN₃ = 628.57) Sub 1(21) m/z = 473.08(C₃₀H₂₀BrN = 474.40) Sub 1(22) m/z = 474.96(C₂₄H₁₅Br₂N = 477.20) Sub 1(23) m/z = 550.99(C₃₀H₁₉Br₂N = 553.30) Sub 1(24) m/z = 580.94(C₃₀H₁₇Br₂N = 580.34) Sub 1(25) m/z = 477.94(C₂₁H₁₂Br₂N₄ = 480.16) Sub 1(26) m/z = 630.01(C₃₃H₂₀Br₂N₄ = 632.36) Sub 1(27) m/z = 574.99(C₃₂H₁₉Br₂N = 577.32) Sub 1(28) m/z = 550.99(C₃₀H₁₉Br₂N = 553.30) Sub 1(29) m/z = 524.97(C₂₈H₁₇Br₂N = 527.26) Sub 1(30) m/z = 524.97(C₂₈H₁₇Br₂N = 527.26) Sub 1(31) m/z = 574.99(C₃₂H₁₉Br₂N = 577.32) Sub 1(32) m/z = 513.11(C₃₃H₂₄BrN = 514.47)

Synthesis Examples of Sub 2

Sub 2 of reaction scheme 1 can be synthesized by the reaction path of reaction scheme 3 below, but is not limited thereto.

Synthesis Examples of Sub 2-1

Bromobenzene (37.1 g, 236.2 mmol) was added to a round bottom flask and dissolved in toluene (2200 mL), aniline (20 g, 214.8 mmol), Pd₂(dba)₃ (9.83 g, 10.7 mmol), P(t-Bu)₃ (4.34 g, 21.5 mmol), NaOt-Bu (62 g, 644.3 mmol) were added in the order and stirred at 100° C. After the reaction was completed, the reaction mixture was extracted with ether and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 28 g of the product. (yield: 77%)

Synthesis Examples of Sub 2-13

3-bromodibenzo[b,d]thiophene (42.8 g, 162.5 mmol), toluene(1550 mL), [1,1′-biphenyl]-4-amine (25 g, 147.7 mmol), Pd₂(dba)₃ (6.76 g, 7.4 mmol), P(t-Bu)₃ (3 g, 14.8 mmol), NaOt-Bu (42.6 g, 443.2 mmol) were added, the same procedure as described in the synthesis method of the 2-1 was carried out to obtain 37.9 g of the product. (yield: 73%). Examples of Sub 2 include, but are not limited to, the followings.

TABLE 2 compound FD-MS compound FD-MS Sub 2-1 m/z = 169.09(C₁₂H₁₁N = 169.22) Sub 2-2 m/z = 245.12(C₁₈H₁₅N = 245.32) Sub 2-3 m/z = 245.12(C₁₈H₁₅N = 245.32) Sub 2-4 m/z = 321.15(C₂₄H₁₉N = 321.41) Sub 2-5 m/z = 321.15 (C₂₄H₁₉N = 321.41) Sub 2-6 m/z = 269.12(C₂₀H₁₅N = 269.34) Sub 2-7 m/z = 269.12(C₂₀H₁₅N = 269.34) Sub 2-8 m/z = 295.14(C₂₂H₁₇N = 295.38) Sub 2-9 m/z = 409.18(C₃₁H₂₃N = 409.52) Sub 2-10 m/z = 483.20(C₃₇H₂₅N = 483.60) Sub 2-11 m/z = 459.20(C₃₅H₂₅N = 459.58) Sub 2-12 m/z = 485.21(C₃₇H₂₇N = 485.62) Sub 2-13 m/z = 275.08(C₁₈H₁₃NS = 275.37) Sub 2-14 m/z = 335.13(C₂₄H₁₇NO = 335.40) Sub 2-15 m/z = 297.13(C₂₀H₁₅N₃ = 297.35) Sub 2-16 m/z = 219.10(C₁₆H₁₃N = 219.28) Sub 2-17 m/z = 249.12(C₁₇H₁₅NO = 249.31) Sub 2-18 m/z = 197.12(C₁₄H₁₅N = 197.28) Sub 2-19 m/z = 229.11(C₁₄H₁₅NO₂ = 229.27) Sub 2-20 m/z = 174.12(C₁₂H₆D₅N = 174.25) Sub 2-21 m/z = 281.21(C₂₀H₂₇N = 281.44) Sub 2-22 m/z = 321.15(C₂₄H₁₉N = 321.41) Sub 2-23 m/z = 321.15(C₂₄H₁₉N = 321.41) Sub 2-24 m/z = 321.15(C₂₄H₁₉N = 321.41) Sub 2-25 m/z = 321.15(C₂₄H₁₉N = 321.41) Sub 2-26 m/z = 321.15(C₂₄H₁₉N = 321.41) Sub 2-27 m/z = 297.13(C₂₀H₁₅N₃ = 297.35) Sub 2-28 m/z = 499.20(C₃₆H₂₅N₃ = 499.60) Sub 2-29 m/z = 499.20(C₃₆H₂₂N₂ = 410.51) Sub 2-30 m/z = 424.16(C₃₀H₂₀N₂O = 424.49) Sub 2-31 m/z = 440.13(C₃₀H₂₀N₂S = 440.56) Sub 2-32 m/z = 384.16(C₂₈H₂₀N₂ = 384.47) Sub 2-33 m/z = 334.15(C₂₄H₁₈N₂ = 334.41) Sub 2-34 m/z = 450.21(C₃₃H₂₆N₂ = 450.57) Sub 2-35 m/z = 410.18(C₃₀H₂₂N₂ = 410.51) Sub 2-36 m/z = 410.18(C₃₀H₂₂N₂ = 410.51) Sub 2-37 m/z = 575.24(C₄₂H₂₉N₃ = 575.70) Sub 2-38 m/z = 574.24(C₄₃H₃₀N₂ = 574.71) Sub 2-39 m/z = 460.19(C₃₄H₂₄N₂ = 460.57) Sub 2-40 m/z = 460.19(C₃₄H₂₄N₂ = 460.57) Sub 2-41 m/z = 461.19(C₃₃H₂₃N₃ = 461.56) Sub 2-42 m/z = 626.27(C₄₇H₃₄N₂ = 626.79) Sub 2-43 m/z = 565.23(C₃₉H₂₇N₅ = 565.67) Sub 2-44 m/z = 415.21(C₃₀H₁₇D₅N₂ = 415.54) Sub 2-45 m/z = 486.21(C₃₆H₂₆N₂ = 486.61) Sub 2-46 m/z = 415.21(C₃₀H₁₇D₅N₂ = 415.54)

Synthesis Examples of Final Products 1 Synthesis Examples of 1-37

Sub 2-1 (8.0 g, 47.3 mmol) was added in a round bottom flask and dissolved in toluene (500 mL), Sub 1(6) (20.7 g, 52.0 mmol), Pd₂(dba)₃ (2.4 g, 2.6 mmol), P(t-Bu)₃ (1.05 g, 5.2 mmol), NaOt-Bu (13.6 g, 141.8 mmol) were added and stirred at 100° C. After the reaction was completed, the reaction mixture was extracted with CH₂Cl₂ and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 16.1 g of the product. (yield: 70%)

Synthesis Examples of 1-10

Sub 2-35 (19.4 g, 47.3 mmol), toluene (500 mL), Sub 1(5) (20.7 g, 52.0 mmol), Pd₂(dba)₃ (2.4 g, 2.6 mmol), P(t-Bu)₃ (1.05 g, 5.2 mmol), NaOt-Bu (13.6 g, 141.8 mmol) were added, the same procedure as described in the synthesis method of the 1-37 was carried out to obtain 24.1 g of the product 1-10. (yield: 70%).

Synthesis Examples of 1-54

Synthesis Method of Inter_A-1

Sub 2-2 (11.6 g, 47.3 mmol), toluene (500 mL), Sub 1(22) (24.8 g, 52.0 mmol), Pd₂(dba)₃ (2.4 g, 2.6 mmol), P(t-Bu)₃ (1.05 g, 5.2 mmol), NaOt-Bu (13.6 g, 141.8 mmol) were added, the same procedure as described in the synthesis method of the 1-37 was carried out to obtain 22.8 g of the product Inter_A-1. (yield: 75%).

Synthesis Method of 1-54

Sub 2-13 (8 g, 29.05 mmol), Inter_A-1 (20.5 g, 32 mmol), toluene (305 mL), Pd₂(dba)₃ (1.5 g, 1.6 mmol), P(t-Bu)₃ (0.65 g, 3.2 mmol), NaOt-Bu (8.4 g, 87.2 mmol) were added, the same procedure as described in the synthesis method of the 1-37 was carried out to obtain 18 g of the product 1-54. (yield: 74%).

Synthesis Examples of 2-5

Sub 2-46 (7.2 g, 20 mmol), Sub 1(33) (8.73 g, 22 mmol), Pd₂(dba)₃ (1 g, 1.1 mmol), P(t-Bu)₃ (0.4 g, 2.2 mmol), NaOt-Bu (5.74 g, 60 mmol), toluene (210 mL) were added, the same procedure as described in the synthesis method of the 1-37 was carried out to obtain 11.5 g of the product 2-5. (yield: 85%).

Synthesis Examples of 2-18

Sub 2-12 (9.7 g, 20 mmol), Sub 1(34) (12.2 g, 22 mmol), Pd₂(dba)₃ (1.0 g, 1.1 mmol), P(t-Bu)₃ (0.4 g, 2.2 mmol), NaOt-Bu (5.8 g, 60 mmol), toluene (210 mL) were added, the same procedure as described in the synthesis method of the 1-37 was carried out to obtain 15.5 g of the product 2-18. (yield: 81%).

Synthesis Examples of 2-60

Sub 1(35) (13.9 g, 24.1 mmol), Sub 2-16 (6.3 g, 28.9 mmol), Pd₂(dba)₃ (2.2 g, 2.4 mmol), P(t-Bu)₃ (1 g, 4.8 mmol), NaOt-Bu (8.3 g, 86.7 mmol), toluene (260 mL) were added, the same procedure as described in the synthesis method of the 1-37 was carried out to obtain 16.5 g of the product 2-60. (yield: 80%).

TABLE 3 compound FD-MS compound FD-MS 1-1 m/z = 562.24(C₄₂H₃₀N₂ = 562.72) 1-2 m/z = 602.27(C₄₅H₃₄N₂ = 602.78) 1-3 m/z = 563.24(C₄₁H₂₉N₃ = 563.70) 1-4 m/z = 714.30(C₅₄H₃₈N₂ = 714.91) 1-5 m/z = 678.30(C₅₁H₃₈N₂ = 678.88) 1-6 m/z = 802.33(C₆₁H₄₂N₂ = 803.02) 1-7 m/z = 800.32(C₆₁H₄₀N₂ = 801.01) 1-8 m/z = 563.24(C₄₁H₂₉N₃ = 563.70) 1-9 m/z = 668.23(C₄₈H₃₂N₂S = 668.86) 1-10 m/z = 727.30(C₅₄H₃₇N₃ = 727.91) 1-11 m/z = 652.25(C₄₈H₃₂N₂O = 652.80) 1-12 m/z = 662.27(C₅₀H₃₄N₂ = 662.84) 1-13 m/z = 536.23(C₄₀H₂₈N₂ = 536.68) 1-14 m/z = 586.24(C₄₄H₃₀N₂ = 586.74) 1-15 m/z = 712.29(C₅₄H₃₆N₂ = 712.90) 1-16 m/z = 714.30(C₅₄H₃₈N₂ = 714.91) 1-17 m/z = 754.33(C₅₇H₄₂N₂ = 754.98) 1-18 m/z = 957.38(C₇₀H₄₇N₅ = 958.18) 1-19 m/z = 965.38(C₇₃H₄₇N₃ = 966.20) 1-20 m/z = 719.24(C₅₁H₃₃N₃S = 719.91) 1-21 m/z = 758.24(C₅₄H₃₄N₂OS = 758.94) 1-22 m/z = 893.38(C₆₇H₄₇N₃ = 894.13) 1-23 m/z = 652.25(C₄₈H₃₂N₂O = 652.80) 1-24 m/z = 662.27(C₅₀H₃₄N₂ = 662.84) 1-25 m/z = 562.24(C₄₂H₃₀N₂ = 562.72) 1-26 m/z = 612.26(C₄₆H₃₂N₂ = 612.78) 1-27 m/z = 688.29(C₅₂H₃₆N₂ = 688.87) 1-28 m/z = 714.30(C₅₄H₃₈N₂ = 714.91) 1-29 m/z = 754.33(C₅₇H₄₂N₂ = 754.98) 1-30 m/z = 878.37(C₆₇H₄₆N₂ = 879.12) 1-31 m/z = 876.35(C₆₇H₄₄N₂ = 877.10) 1-32 m/z = 639.27(C₄₇H₃₃N₃ = 369.80) 1-33 m/z = 768.26(C₅₆H₃₆N₂S = 768.98) 1-34 m/z = 833.29(C₆₀H₃₉N₃S = 834.05) 1-35 m/z = 742.26(C₅₄H₃₄N₂O_(s) = 742.88) 1-36 m/z = 778.333(C₅₉H₄₂N₂ = 779.00) 1-37 m/z = 486.21(C₃₆H₂₆N₂ = 486.62) 1-38 m/z = 536.23(C₄₀H₂₈N₂ = 536.68) 1-39 m/z = 612.26(C₄₆H₃₂N₂ = 612.78) 1-40 m/z = 638.27(C₄₈H₃₄N₂ = 638.81) 1-41 m/z = 491.24(C₃₆H₂₁D₅N₂ = 491.65) 1-42 m/z = 612.26(C₄₆H₃₂N₂ = 612.78) 1-43 m/z = 794.28(C₅₈H₃₈N₂S = 795.02) 1-44 m/z = 656.26(C₄₈H₃₃FN₂ = 656.80) 1-45 m/z = 717.29(C₅₁H₃₅N₅ = 717.88) 1-46 m/z = 728.32(C₅₅H₄₀N₂ = 728.94) 1-47 m/z = 842.34(C₆₂H₄₂N₄ = 843.05) 1-48 m/z = 714.30(C₅₄H₃₈N₂ = 714.91) 1-49 m/z = 653.28(C₄₈H₃₅N₃ = 653.81) 1-50 m/z = 703.30(C₅₂H₃₇N₃ = 703.87) 1-51 m/z = 805.35(C₆₀H₄₃N₃ = 806.00) 1-52 m/z = 753.31(C₅₆H₃₉N₃ = 753.93) 1-53 m/z = 818.34(C₆₀H₄₂N₄ = 819.00) 1-54 m/z = 835.30(C₆₀H₄₁N₃S = 836.05) 1-55 m/z = 655.27(C₄₆H₃₃N₅ = 655.79) 1-56 m/z = 885.32(C₆₄H₄₃N₃S = 886.11) 1-57 m/z = 759.27(C₅₄H₃₇N₃S = 759.96) 1-58 m/z = 706.28(C₄₉H₃₄N₆ = 706.83) 1-59 m/z = 960.39(C₆₉H₄₈N₆ = 961.16) 1-60 m/z = 853.35(C₆₄H₄₃N₃ = 854.05) 1-61 m/z = 894.37(C₆₆H₄₆N₄ = 895.10) 1-62 m/z = 834.38(C₆₂H₃₈D₅N₃ = 835.06) 1-63 m/z = 855.36(C₆₄H₄₅N₃ = 856.06) 1-64 m/z = 853.35(C₆₄H₄₃N₃ = 854.05) 1-65 m/z = 794.37(C₆₀H₄₆N₂ = 795.04) 1-66 m/z = 987.39(C₇₁H₄₉N₅O = 988.21) 1-67 m/z = 1021.44(C₇₇H₅₅N₃ = 1022.31) 1-68 m/z = 737.23(C₅₁H₃₂FN₃S = 737.90) 2-1 m/z = 562.24(C₄₂H₃₀N₂ = 562.72) 2-2 m/z = 602.27(C₄₅H₃₄N₂ = 602.78) 2-3 m/z = 563.24(C₄₁H₂₉N₃ = 563.70) 2-4 m/z = 714.30(C₅₄H₃₈N₂ = 714.91) 2-5 m/z = 678.30(C₅₁H₃₈N₂ = 678.88) 2-6 m/z = 802.33(C₆₁H₄₂N₂ = 803.02) 2-7 m/z = 800.32(C₆₁H₄₀N₂ = 801.01) 2-8 m/z = 563.24(C₄₁H₂₉N₃ = 563.70) 2-9 m/z = 668.23(C₄₈H₃₂N₂S = 668.86) 2-10 m/z = 727.30(C₅₄H₃₇N₃ = 727.91) 2-11 m/z = 652.25(C₄₈H₃₂N₂O = 652.80) 2-12 m/z = 662.27(C₅₀H₃₄N₂ = 662.84) 2-13 m/z = 536.23(C₄₀H₂₈N₂ = 536.68) 2-14 m/z = 586.24(C₄₄H₃₀N₂ = 586.74) 2-15 m/z = 712.29(C₅₄H₃₆N₂ = 712.90) 2-16 m/z = 714.30(C₅₄H₃₈N₂ = 714.91) 2-17 m/z = 754.33(C₅₇H₄₂N₂ = 754.98) 2-18 m/z = 957.38(C₇₀H₄₇N₅ = 958.18) 2-19 m/z = 965.38(C₇₃H₄₇N₃ = 966.20) 2-20 m/z = 719.24(C₅₁H₃₃N₃S = 719.91) 2-21 m/z = 758.24(C₅₄H₃₄N₂OS = 758.94) 2-22 m/z = 893.38(C₆₇H₄₇N₃ = 894.13) 2-23 m/z = 652.25(C₄₈H₃₂N₂O = 652.80) 2-24 m/z = 662.27(C₅₀H₃₄N₂ = 662.84) 2-25 m/z = 562.24(C₄₂H₃₀N₂ = 562.72) 2-26 m/z = 612.26(C₄₆H₃₂N₂ = 612.78) 2-27 m/z = 688.29(C₅₂H₃₆N₂ = 688.87) 2-28 m/z = 714.30(C₅₄H₃₈N₂ = 714.91) 2-29 m/z = 754.33(C₅₇H₄₂N₂ = 754.98) 2-30 m/z = 878.37(C₆₇H₄₆N₂ = 879.12) 2-31 m/z = 876.35(C₆₇H₄₄N₂ = 877.10) 2-32 m/z = 639.27(C₄₇H₃₃N₃ = 369.80) 2-33 m/z = 768.26(C₅₆H₃₆N₂S = 768.98) 2-34 m/z = 833.29(C₆₀H₃₉N₃S = 834.05) 2-35 m/z = 742.26(C₅₄H₃₄N₂O_(s) = 742.88) 2-36 m/z = 778.333(C₅₉H₄₂N₂ = 779.00) 2-37 m/z = 486.21(C₃₆H₂₆N₂ = 486.62) 2-38 m/z = 536.23(C₄₀H₂₈N₂ = 536.68) 2-39 m/z = 612.26(C₄₆H₃₂N₂ = 612.78) 2-40 m/z = 638.27(C₄₈H₃₄N₂ = 638.81) 2-41 m/z = 491.24(C₃₆H₂₁D₅N₂ = 491.65) 2-42 m/z = 612.26(C₄₆H₃₂N₂ = 612.78) 2-43 m/z = 794.28(C₅₈H₃₈N₂S = 795.02) 2-44 m/z = 656.26(C₄₈H₃₃FN₂ = 656.80) 2-45 m/z = 717.29(C₅₁H₃₅N₅ = 717.88) 2-46 m/z = 728.32(C₅₅H₄₀N₂ = 728.94) 2-47 m/z = 842.34(C₆₂H₄₂N₄ = 843.05) 2-48 m/z = 714.30(C₅₄H₃₈N₂ = 714.91) 2-49 m/z = 653.28(C₄₈H₃₅N₃ = 653.81) 2-50 m/z = 703.30(C₅₂H₃₇N₃ = 703.87) 2-51 m/z = 805.35(C₆₀H₄₃N₃ = 806.00) 2-52 m/z = 753.31(C₅₆H₃₉N₃ = 753.93) 2-53 m/z = 818.34(C₆₀H₄₂N₄ = 819.00) 2-54 m/z = 835.30(C₆₀H₄₁N₃S = 836.05) 2-55 m/z = 655.27(C₄₆H₃₃N₅ = 655.79) 2-56 m/z = 885.32(C₆₄H₄₃N₃S = 886.11) 2-57 m/z = 759.27(C₅₄H₃₇N₃S = 759.96) 2-58 m/z = 706.28(C₄₉H₃₄N₆ = 706.83) 2-59 m/z = 960.39(C₆₉H₄₈N₆ = 961.16) 2-60 m/z = 853.35(C₆₄H₄₃N₃ = 854.05) 2-61 m/z = 894.37(C₆₆H₄₆N₄ = 895.10) 2-62 m/z = 834.38(C₆₂H₃₈D₅N₃ = 835.06) 2-63 m/z = 855.36(C₆₄H₄₅N₃ = 856.06) 2-64 m/z = 853.35(C₆₄H₄₃N₃ = 854.05) 2-65 m/z = 794.37(C₆₀H₄₆N₂ = 795.04) 2-66 m/z = 987.39(C₇₁H₄₉N₅O = 988.21) 2-67 m/z = 1021.44(C₇₇H₅₅N₃ = 1022.31) 2-68 m/z = 737.23(C₅₁H₃₂FN₃S = 737.90)

Synthesis Examples 2

The final product 2 represented by Formula (1) of the present invention is prepared by reacting Sub 3 and Sub 4 as shown in Reaction Scheme 4 below.

Synthesis Example of Sub 3

Sub 3 of Reaction Scheme 4 can be synthesized by the reaction path of Reaction Scheme 5 below, but is not limited thereto.

Synthesis Examples of Sub 3(1)

Synthesis Method of Sub 3-2-1

After 5-bromobenzo[b]naphtha[1,2-d]thiophene (50 g, 155 mmol), bis(pinacolato)diboron (43.4 g, 171 mmol), KOAc (46 g, 466 mmol), PdCl₂(dppf) (3.8 g, 4.7 mmol) were dissolved in DMF (980 mL), and refluxed at 120° C. for 12 hours. When the reaction was completed, the temperature of the reaction was cooled to room temperature, extracted with CH₂Cl₂ and wiped with water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was recrystallized by CH₂Cl₂ and methanol solvent to obtain Sub 3-2-1. (45 g, 80%)

Synthesis Method of Sub 3-4-1

Sub 3-2-1 (40 g, 111 mmol), bromo-2-nitrobenzene (33.5 g, 133 mmol), K₂CO₃ (46.03 g, 333 mmol), Pd(PPh₃)₄(7.7 g, 6.66 mmol) were added in a round bottom flask and THF (490 mL) and water (245 mL) were added to dissolve and refluxed at 80° C. for 12 hours. When the reaction was completed, the temperature of the reaction was cooled to room temperature, extracted with CH₂Cl₂ and wiped with water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography to obtain Sub 3-4-1. (33.3 g, 74%)

Synthesis Method of Sub 3(1)

Sub 3-4-1 (22.8 g, 56.3 mmol) and triphenylphosphine (37 g, 141 mmol) were dissolved in o-dichlorobenzene (235 mL) and refluxed for 24 hours. When the reaction was completed, the solvent was removed using reduced pressure distillation. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain Sub 3(1). (16.4 g, 78%)

Synthesis Example of Sub 3(2)

Synthesis Method of Sub 3-2-2

5-bromobenzo[b]naphtho[2,1-d]thiophene (46.1 g, 155 mmol) was carried out in the same manner as in Sub 3-2-1 to give the product Sub 3-2-2 (43.2 g, 80%).

Synthesis Method of Sub 3-4-2

Sub 3-2-2 (38.2 g, 111 mmol), and 2-bromo-1-nitronaphthalene (33.5 g, 133 mmol) were carried out in the same manner as in Sub 3-4-1 to give the product Sub 3-4-2 (32.4 g, 75%).

Synthesis Method of Sub 3(2)

Sub 3-4-2 (21.9 g, 56.3 mmol) was carried out in the same manner as in Sub 3(1) to give the product Sub 3(2) (14.9 g, 78%).

Synthesis Example of Sub 3(3)

Synthesis Method of Sub 3-2-3

2-(5-bromobenzo[b]naphtho[1,2-d]thiophen-10-yl)-9-phenyl-9H-carbazole (85.9 g, 155 mmol) was carried out in the same manner as in Sub 3-2-1 to give the product Sub 3-2-3 (72.7 g, 78%).

Synthesis Method of Sub 3-4-3

Sub 3-2-3 (66.8 g, 111 mmol) and 2-bromo-1-nitronaphthalene (33.5 g, 133 mmol) were carried out in the same manner as in Sub 3-4-1 to give the product Sub 3-4-3 (55.3 g, 77%).

Synthesis Method of Sub 3(3)

Sub 3-4-3 (36.4 g, 56.3 mmol) was carried out in the same manner as in Sub 3(1) to give the product Sub 3(3) (27.3 g, 79%).

Examples of Sub 3 include, but are not limited to, the followings.

TABLE 4 compound FD-MS compound FD-MS Sub 3(1) m/z = 373.09(C₂₆H₁₅NS = 373.47) Sub 3(2) m/z = 357.12(C₂₆H₁₅NO = 357.41) Sub 3(3) m/z = 614.18(C₄₄H₂₆N₂S = 614.77) Sub 3(4) m/z = 429.16(C₃₀H₂₃NS = 429.58) Sub 3(5) m/z = 377.12(C₂₆H₁₁D₄NS = 377.50) Sub 3(6) m/z = 604.17(C₄₁H₂₄N₄S = 604.73) Sub 3(7) m/z = 449.12(C₃₂H₁₉NS = 449.57) Sub 3(8) m/z = 429.16(C₃₀H₂₃NS = 429.58) Sub 3(9) m/z = 391.08(C₂₆H₁₄FNS = 391.46) Sub 3(10) m/z = 449.12(C₃₂H₁₉NS = 449.57) Sub 3(11) m/z = 433.15(C₃₂H₁₉NO = 433.51) Sub 3(12) m/z = 598.20(C₄₄H₂₆N₂O = 598.71) Sub 3(13) m/z = 413.18(C₃₀H₂₃NO = 413.52) Sub 3(14) m/z = 361.14(C₂₆H₁₁D₄NO = 361.44) Sub 3(15) m/z = 588.20(C₄₁H₂₄N₄O = 588.67) Sub 3(16) m/z = 433.15(C₃₂H₁₉NO = 433.51)

Examples of Sub 4

Examples of Sub 4 include, but are not limited to, the followings.

TABLE 5 compound FD-MS compound FD-MS Sub 4-1 m/z = 155.96(C₆H₅Br = 157.01) Sub 4-2 m/z = 205.97(C₁₀H₇Br = 207.07) Sub 4-3 m/z = 205.97(C₁₀H₇Br = 207.07) Sub 4-4 m/z = 231.99(C₁₂H₉Br = 233.10) Sub 4-5 m/z = 309.02(C₁₇H₁₂BrN = 310.19) Sub 4-6 m/z = 311.01(C₁₅H₁₀BrN₃ = 312.16) Sub 4-7 m/z = 310.01(C₁₆H₁₁BrN₂ = 311.18) Sub 4-8 m/z = 310.01(C₁₆H₁₁BrN₂ = 311.18) Sub 4-9 m/z = 310.01(C₁₆H₁₁BrN₂ = 311.18) Sub 4-10 m/z = 387.04(C₂₁H₁₄BrN₃ = 388.26) Sub 4-11 m/z = 386.04(C₂₂H₁₅BrN₂ = 387.27) Sub 4-12 m/z = 386.04(C₂₂H₁₅BrN₂ = 387.27) Sub 4-13 m/z = 348.03(C₁₉H₁₃BrN₂ = 349.22) Sub 4-14 m/z = 271.99(C₁₃H₉BrN₂ = 273.13) Sub 4-15 m/z = 283.99(C₁₄H₉BrN₂ = 285.14) Sub 4-16 m/z = 374.01(C₂₀H₁₁BrN₂O = 375.22) Sub 4-17 m/z = 400.06(C₂₃H₁₇BrN₂ = 401.30) Sub 4-18 m/z = 360.03(C₂₀H₁₃BrN₂ = 361.23) Sub 4-19 m/z = 476.09(C₂₉H₂₁BrN₂ = 477.39) Sub 4-20 m/z = 284.99(C₁₃H₈BrN₃ = 286.13) Sub 4-21 m/z = 289.03(C₁₄H₄D₅BrN₂ = 290.2) Sub 4-22 m/z = 284.99(C₁₃H₈BrN₃ = 286.13) Sub 4-23 m/z = 375.00(C₁₉H₁₀BrN₃O = 376.2) Sub 4-24 m/z = 401.05(C₂₂H₁₆BrN₃ = 402.29) Sub 4-25 m/z = 296.02(C₁₆H₉ClN₂S = 296.77) Sub 4-26 m/z = 322.03(C₁₈H₁₁ClN₂S = 322.81) Sub 4-27 m/z = 322.03(C₁₈H₁₁ClN₂S = 322.81) Sub 4-28 m/z = 168.98(C₇H₄ClNS = 169.63) Sub 4-29 m/z = 168.98(C₇H₄ClNS = 169.63)) Sub 4-30 m/z = 169.97(C₆H₃ClN₂S = 170.62) Sub 4-31 m/z = 246.00(C₁₂H₇ClN₂S = 246.72) Sub 4-32 m/z = 322.03(C₁₈H₁₁ClN₂S = 322.81) Sub 4-33 m/z = 322.03(C₁₈H₁₁ClN₂S = 322.81) Sub 4-34 m/z = 168.98(C₇H₄ClNS = 169.63) Sub 4-35 m/z = 168.98(C₇H₄ClNS = 169.63)) Sub 4-36 m/z = 169.97(C₆H₃ClN₂S = 170.62) Sub 4-37 m/z = 229.04(C₁₂H₈ClN₃ = 229.67) Sub 4-38 m/z = 279.06(C₁₆H₁₀ClN₃ = 279.72) Sub 4-39 m/z = 305.07(C₁₈H₁₂ClN₃ = 305.76) Sub 4-40 m/z = 228.05(C₁₃H₉ClN₂ = 228.68) Sub 4-41 m/z = 228.05(C₁₃H₉ClN₂ = 228.68) Sub 4-42 m/z = 229.04(C₁₂H₈ClN₃ = 229.67) Sub 4-43 m/z = 229.04(C₁₂H₈ClN₃ = 229.67) Sub 4-44 m/z = 279.06(C₁₆H₁₀ClN₃ = 279.72) Sub 4-45 m/z = 305.07(C₁₈H₁₂ClN₃ = 305.76) Sub 4-46 m/z = 228.05(C₁₃H₉ClN₂ = 228.68) Sub 4-47 m/z = 228.05(C₁₃H₉ClN₂ = 228.68) Sub 4-48 m/z = 229.04(C₁₂H₈ClN₃ = 229.67) Sub 4-49 m/z = 330.1(C₂₀H₁₁ClN₂O = 330.77) Sub 4-50 m/z = 372.05(C₂₂H₁₃ClN₂S = 372.87) Sub 4-51 m/z = 366.09(C₂₄H₁₅ClN₂ = 366.85) Sub 4-52 m/z = 340.08(C₂₂H₁₃ClN₂ = 340.81) Sub 4-53 m/z = 290.06(C₁₈H₁₁ClN₂ = 290.75) Sub 4-54 m/z = 340.08(C₂₂H₁₃ClN₂ = 340.81)

Synthesis Example of Final Products 2 Synthesis Example of 3-1

After Sub 3(2) (169 g, 47.3 mmol) was added in a round bottom flask and dissolved in toluene (500 mL), Sub 4-2 (8.2 g, 52.0 mmol), Pd₂(dba)₃ (2.4 g, 2.6 mmol), P(t-Bu)₃ (1.1 g, 5.2 mmol), NaOt-Bu (15 g, 156.1 mmol) were added and stirred at 100° C. After the reaction was completed, the reaction mixture was extracted with CH₂Cl₂ and water. The organic layer was dried over MgSO₄ and concentrated. The resulting compound was separated by silicagel column chromatography and recrystallized to obtain 14.6 g of the product. (yield: 71%)

Synthesis Example of 3-5

After Sub 3(2)(16.9 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-55(8.4 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 14.3 g (yield: 69%).

Synthesis Example of 3-11

After Sub 3(2)(16.9 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-56(12.8 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 18.1 g (yield: 73%).

Synthesis Example of 3-35

After Sub 3(2)(16.9 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-57(18.8 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 21.7 g (yield: 72%).

Synthesis Example of 3-48

After Sub 3(2)(16.9 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-58(8.2 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 14.6 g (yield: 71%).

Synthesis Example of 3-65

After Sub 3(2)(16.9 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-59(26.3 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 25.6 g (yield: 69%).

Synthesis Example of 3-79

After Sub 3(2)(16.9 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-60(19.5 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 20.3 g (yield: 66%).

Synthesis Example of 3-90

After Sub 3(16)(20.5 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-15(14.8 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 20.5 g (yield: 68%).

Synthesis Example of 4-6

After Sub 3(1)(17.7 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-61(16.1 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 20.8 g (yield: 73%).

Synthesis Example of 4-23

After Sub 3(1)(17.7 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-6(16.2 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 21.5 g (yield: 75%).

Synthesis Example of 4-32

After Sub 3(1)(17.7 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-15(14.8 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 19.9 g (yield: 73%).

Synthesis Example of 4-51

After Sub 3(1)(17.7 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-63(21.4 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 23.0 g (yield: 69%).

Synthesis Example of 4-61

After Sub 3(1)(17.7 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-25(15.4 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 21.3 g (yield: 71%).

Synthesis Example of 4-73

After Sub 3(1)(17.7 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-62(25.5 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 23.7 g (yield: 64%).

Synthesis Example of 4-86

After Sub 3(3)(29.1 g, 47.3 mmol) was placed in a round bottom flask and dissolved in toluene (500 mL), Sub 4-1(8.2 g, 52.0 mmol) was added thereto, and was carried out in the same manner as 3-1 to give the product 21.2 g (yield: 65%).

TABLE 6 compound FD-MS compound FD-MS 3-1 m/z = 433.15(C₃₂H₁₉NO = 433.51) 3-2 m/z = 483.16(C₃₆H₂₁NO = 483.57) 3-3 m/z = 483.16(C₃₆H₂₁NO = 483.57) 3-4 m/z = 509.18(C₃₈H₂₃NO = 509.61) 3-5 m/z = 438.18(C₃₂H₁₄D₅NO = 438.54) 3-6 m/z = 585.21(C₄₄H₂₇NO = 585.71) 3-7 m/z = 583.19(C₄₄H₂₅NO = 583.69) 3-8 m/z = 533.18(C₄₀H₂₃NO = 533.63) 3-9 m/z = 598.20(C₄₄H₂₆N₂O = 598.71) 3-10 m/z = 539.13(C₃₈H₂₁NOS = 539.65) 3-11 m/z = 523.16(C₃₈H₂₁NO₂ = 523.59) 3-12 m/z = 549.21(C₄₁H₂₇NO = 549.67) 3-13 m/z = 673.24(C₅₁H₃₁NO = 673.82) 3-14 m/z = 671.22(C₅₁H₂₉NO = 671.80) 3-15 m/z = 434.14(C₃₁H₁₈N₂O = 434.50) 3-16 m/z = 434.14(C₃₁H₁₈N₂O = 434.50) 3-17 m/z = 434.14(C₃₁H₁₈N₂O = 434.50) 3-18 m/z = 435.14(C₃₀H₁₇N₃O = 435.49) 3-19 m/z = 435.14(C₃₀H₁₇N₃O = 435.49) 3-20 m/z = 435.14(C₃₀H₁₇N₃O = 435.49) 3-21 m/z = 436.13(C₂₉H₁₆N₄O = 436.47) 3-22 m/z = 586.20(C₄₃H₂₆N₂O = 586.69) 3-23 m/z = 588.20(C₄₁H₂₄N₄O = 588.67) 3-24 m/z = 587.20(C₄₂H₂₅N₃O = 587.68) 3-25 m/z = 587.20(C₄₂H₂₅N₃O = 587.68) 3-26 m/z = 587.20(C₄₂H₂₅N₃O = 587.68) 3-27 m/z = 664.23(C₄₇H₂₈N₄O = 664.77) 3-28 m/z = 663.23(C₄₈H₂₉N₃O = 663.78) 3-29 m/z = 663.23(C₄₈H₂₉N₃O = 663.78) 3-30 m/z = 625.22(C₄₅H₂₇N₃O = 625.73) 3-31 m/z = 549.18(C₃₉H₂₃N₃O = 549.63) 3-32 m/z = 561.18(C₄₀H₂₃N₃O = 561.64) 3-33 m/z = 611.20(C₄₄H₂₅N₃O = 611.70) 3-34 m/z = 611.20(C₄₄H₂₅N₃O = 611.70) 3-35 m/z = 637.22(C₄₆H₂₇N₃O = 637.74) 3-36 m/z = 566.22(C₄₀H₁₈D₅N₃O = 566.7) 3-37 m/z = 661.22(C₄₈H₂₇N₃O = 661.76) 3-38 m/z = 667.17(C₄₆H₂₅N₃OS = 667.79) 3-39 m/z = 651.19(C₄₆H₂₅N₃O₂ = 651.73) 3-40 m/z = 726.24(C₅₂H₃₀N₄O = 726.84) 3-41 m/z = 717.19(C₅₀H₂₇N₃OS = 717.85) 3-42 m/z = 637.22(C₄₆H₂₇N₃O = 637.74) 3-43 m/z = 743.20(C₅₂H₂₉N₃OS = 743.88) 3-44 m/z = 713.25(C₅₂H₃₁N₃O = 713.84) 3-45 m/z = 484.16(C₃₅H₂₀N₂O = 484.56) 3-46 m/z = 611.20(C₄₄H₂₅N₃O = 611.70) 3-47 m/z = 561.18(C₄₀H₂₃N₃O = 561.64) 3-48 m/z = 661.22(C₄₈H₂₇N₃O = 661.76) 3-49 m/z = 661.22(C₄₈H₂₇N₃O = 661.76) 3-50 m/z = 661.22(C₄₈H₂₇N₃O = 661.76) 3-51 m/z = 687.23(C₅₀H₂₉N₃O = 687.80) 3-52 m/z = 687.23(C₅₀H₂₉N₃O = 687.80) 3-53 m/z = 761.25(C₅₆H₃₁N₃O = 761.88) 3-54 m/z = 767.20(C₅₄H₂₉N₃OS = 767.91) 3-55 m/z = 701.21(C₅₀H₂₇N₃O₂ = 701.79) 3-56 m/z = 776.26(C₅₆H₃₂N₄O = 776.90) 3-57 m/z = 767.20(C₅₄H₂₉N₃OS = 767.91) 3-58 m/z = 737.25(C₅₄H₃₁N₃O = 737.86) 3-59 m/z = 793.22(C₅₆H₃₁N₃OS = 793.94) 3-60 m/z = 763.26(C₅₆H₃₃N₃O = 763.90) 3-61 m/z = 617.16(C₄₂H₂₃N₃OS = 617.73) 3-62 m/z = 667.17(C₄₆H₂₅N₃OS = 667.79) 3-63 m/z = 667.17(C₄₆H₂₅N₃OS = 667.79) 3-64 m/z = 693.19(C₄₈H₂₇N₃OS = 693.82) 3-65 m/z = 782.21(C₅₄H₃₀N₄OS = 782.92) 3-66 m/z = 793.22(C₅₆H₃₁N₃OS = 793.94) 3-67 m/z = 707.17(C₄₈H₂₅N₃O₂S = 707.8) 3-68 m/z = 618.15(C₄₁H₂₂N₄OS = 618.71) 3-69 m/z = 601.18(C₄₂H₂₃N₃O₂ = 601.67) 3-70 m/z = 651.19(C₄₆H₂₅N₃O₂ = 651.73) 3-71 m/z = 651.19(C₄₆H₂₅N₃O₂ = 651.73) 3-72 m/z = 754.24(C₅₃H₃₀N₄O₂ = 754.85) 3-73 m/z = 766.24(C₅₄H₃₀N₄O₂ = 766.86) 3-74 m/z = 701.21(C₅₀H₂₇N₃O₂ = 701.79) 3-75 m/z = 691.19(C₄₈H₂₅N₃O₃ = 691.75) 3-76 m/z = 602.17(C₄₁H₂₂N₄O₂ = 602.65) 3-77 m/z = 617.16(C₄₂H₂₃N₃OS = 617.73) 3-78 m/z = 667.17(C₄₆H₂₅N₃OS = 667.79) 3-79 m/z = 651.19(C₄₆H₂₅N₃O₂ = 651.73) 3-80 m/z = 677.21(C₄₈H₂₇N₃O₂ = 677.76) 3-81 m/z = 782.21(C₅₄H₃₀N₄OS = 782.92) 3-82 m/z = 717.19(C₅₀H₂₇N₃OS = 717.85) 3-83 m/z = 767.22(C₅₄H₂₉N₃O₃ = 767.84) 3-84 m/z = 602.17(C₄₁H₂₂N₄O₂ = 602.65) 3-85 m/z = 664.23(C₄₇H₂₈N₄O = 664.77) 3-86 m/z = 674.24(C₅₀H₃₀N₂O = 674.80) 3-87 m/z = 489.21(C₃₆H₂₇NO = 489.62) 3-88 m/z = 437.17(C₃₂H₁₅D₄NO = 437.53) 3-89 m/z = 664.23(C₄₇H₂₈N₄O = 664.77) 3-90 m/z = 637.22(C₄₆H₂₇N₃O = 637.74) 3-91 m/z = 489.21(C₃₆H₂₇NO = 489.62) 3-92 m/z = 451.14(C₃₂H₁₈FNO = 451.50) 4-1 m/z = 449.12(C₃₂H₁₉NS = 449.57) 4-2 m/z = 499.14(C₃₆H₂₁NS = 499.63) 4-3 m/z = 499.14(C₃₆H₂₁NS = 499.63) 4-4 m/z = 525.16(C₃₈H₂₃NS = 525.67) 4-5 m/z = 454.16(C₃₂H₁₄D₅NS = 454.60) 4-6 m/z = 601.19(C₄₄H₂₇NS = 601.77) 4-7 m/z = 599.17(C₄₄H₂₅NS = 599.75) 4-8 m/z = 549.16(C₄₀H₂₃NS = 549.69) 4-9 m/z = 614.18(C₄₄H₂₆N₂S = 614.77) 4-10 m/z = 555.11(C₃₈H₂₁NS₂ = 555.71) 4-11 m/z = 539.13(C₃₈H₂₁NOS = 539.65) 4-12 m/z = 565.19(C₄₁H₂₇NS = 565.73) 4-13 m/z = 689.22(C₅₁H₃₁NS = 689.88) 4-14 m/z = 687.20(C₅₁H₂₉NS = 687.86) 4-15 m/z = 450.12(C₃₁H₁₈N₂S = 450.56) 4-16 m/z = 450.12(C₃₁H₁₈N₂S = 450.56) 4-17 m/z = 450.12(C₃₁H₁₈N₂S = 450.56) 4-18 m/z = 451.11(C₃₀H₁₇N₃S = 451.55) 4-19 m/z = 451.11(C₃₀H₁₇N₃S = 451.55) 4-20 m/z = 451.11(C₃₀H₁₇N₃S = 451.55) 4-21 m/z = 452.11(C₂₉H₁₆N₄S = 452.54) 4-22 m/z = 602.18(C₄₃H₂₆N₂S = 602.76) 4-23 m/z = 604.17(C₄₁H₂₄N₄S = 604.73) 4-24 m/z = 603.18(C₄₂H₂₅N₃S = 603.74) 4-25 m/z = 603.18(C₄₂H₂₅N₃S = 603.74) 4-26 m/z = 603.18(C₄₂H₂₅N₃S = 603.74) 4-27 m/z = 680.20(C₄₇H₂₈N₄S = 680.83) 4-28 m/z = 679.21(C₄₈H₂₉N₃S = 679.84) 4-29 m/z = 679.21(C₄₈H₂₉N₃S = 679.84) 4-30 m/z = 641.19(C₄₅H₂₇N₃S = 641.79) 4-31 m/z = 565.16(C₃₉H₂₃N₃S = 565.69) 4-32 m/z = 577.16(C₄₀H₂₃N₃S = 577.71) 4-33 m/z = 627.18(C₄₄H₂₅N₃S = 627.77) 4-34 m/z = 627.18(C₄₄H₂₅N₃S = 627.77) 4-35 m/z = 653.19(C₄₆H₂₇N₃S = 653.80) 4-36 m/z = 582.19(C₄₀H₁₈D₅N₃S = 582.74) 4-37 m/z = 677.19(C₄₈H₂₇N₃S = 677.83) 4-38 m/z = 683.15(C₄₆H₂₅N₃S₂ = 683.85) 4-39 m/z = 667.17(C₄₆H₂₅N₃OS = 667.79) 4-40 m/z = 742.22(C₅₂H₃₀N₄S = 742.90) 4-41 m/z = 733.16(C₅₀H₂₇N₃S₂ = 733.91) 4-42 m/z = 653.19(C₄₆H₂₇N₃S = 653.80) 4-43 m/z = 759.18(C₅₂H₂₉N₃S₂ = 759.95) 4-44 m/z = 729.22(C₅₂H₃₁N₃S = 729.90) 4-45 m/z = 500.13(C₃₅H₂₀N₂S = 500.62) 4-46 m/z = 627.18(C₄₄H₂₅N₃S = 627.77) 4-47 m/z = 577.16(C₄₀H₂₃N₃S = 577.71) 4-48 m/z = 677.19(C₄₈H₂₇N₃S = 677.83) 4-49 m/z = 677.19(C₄₈H₂₇N₃S = 677.83) 4-50 m/z = 677.19(C₄₈H₂₇N₃S = 677.83) 4-51 m/z = 703.21(C₅₀H₂₉N₃S = 703.86) 4-52 m/z = 703.21(C₅₀H₂₉N₃S = 703.86) 4-53 m/z = 777.22(C₅₆H₃₁N₃S = 777.95) 4-54 m/z = 783.18(C₅₄H₂₉N₃S₂ = 783.97) 4-55 m/z = 717.19(C₅₀H₂₇N₃OS = 717.85) 4-56 m/z = 792.23(C₅₆H₃₂N₄S = 792.96) 4-57 m/z = 783.18(C₅₄H₂₉N₃S₂ = 783.97) 4-58 m/z = 785.22(C₅₄H₃₁N₃S = 753.92) 4-59 m/z = 809.20(C₅₆H₃₁N₃S₂ = 810.01) 4-60 m/z = 779.24(C₅₆H₃₃N₃S = 779.96) 4-61 m/z = 633.13(C₄₂H₂₃N₃S₂ = 633.79) 4-62 m/z = 683.15(C₄₆H₂₅N₃S₂ = 683.85) 4-63 m/z = 683.15(C₄₆H₂₅N₃S₂ = 683.85) 4-64 m/z = 709.16(C₄₈H₂₇N₃S₂ = 709.89) 4-65 m/z = 798.19(C₅₄H₃₀N₄S₂ = 798.98) 4-66 m/z = 809.20(C₅₆H₃₁N₃S₂ = 810.01) 4-67 m/z = 723.14(C₄₈H₂₅N₃OS₂ = 723.9) 4-68 m/z = 634.13(C₄₁H₂₂N₄S₂ = 634.78) 4-69 m/z = 617.16(C₄₂H₂₃N₃OS = 617.73) 4-70 m/z = 667.17(C₄₆H₂₅N₃OS = 667.79) 4-71 m/z = 667.17(C₄₆H₂₅N₃OS = 667.79) 4-72 m/z = 770.21(C₅₃H₃₀N₄OS = 770.91) 4-73 m/z = 782.21(C₅₄H₃₀N₄OS = 782.92) 4-74 m/z = 717.19(C₅₀H₂₇N₃OS = 717.85) 4-75 m/z = 707.17(C₄₈H₂₅N₃O₂S = 707.8) 4-76 m/z = 618.15(C₄₁H₂₂N₄OS = 618.71) 4-77 m/z = 633.13(C₄₂H₂₃N₃S₂ = 633.79) 4-78 m/z = 683.15(C₄₆H₂₅N₃S₂ = 683.85) 4-79 m/z = 667.17(C₄₆H₂₅N₃OS = 667.79) 4-80 m/z = 693.19(C₄₈H₂₇N₃OS = 693.82) 4-81 m/z = 798.19(C₅₄H₃₀N₄S₂ = 798.98) 4-82 m/z = 733.16(C₅₀H₂₇N₃S₂ = 733.91) 4-83 m/z = 783.20(C₅₄H₂₉N₃O₂S = 783.9) 4-84 m/z = 618.15(C₄₁H₂₂N₄OS = 618.71) 4-85 m/z = 680.20(C₄₇H₂₈N₄S = 680.83) 4-86 m/z = 690.21(C₅₀H₃₀N₂S = 690.86) 4-87 m/z = 505.19(C₃₆H₂₇NS = 505.68) 4-88 m/z = 453.15(C₃₂H₁₅D₄NS = 453.60) 4-89 m/z = 6800.20(C₄₇H₂₈N₄S = 680.83) 4-90 m/z = 653.19(C₄₆H₂₇N₃S = 453.80) 4-91 m/z = 505.19(C₃₆H₂₇NS = 505.68) 4-92 m/z = 467.11(C₃₂H₁₈FNS = 467.56)

Otherwise, the synthesis examples of the present invention represented by Formulas (1) and (20) have been described, but these are all based on the Buchwald-Hartwig cross coupling reaction, Suzuki cross-coupling reaction, Intramolecular acid-induced cyclization reaction (J. mater. Chem. 1999, 9, 2095.), Pd(II)-catalyzed oxidative cyclization reaction (Org. Lett. 2011, 13, 5504), Grignard reaction, Cyclic Dehydration reaction and PPh3-mediated reductive cyclization reaction (J. Org. Chem. 2005, 70, 5014.), and those skilled in the art will readily understand that the above reaction proceeds even when, besides the substituent specified in the specific synthesis example, other substituents(Ar¹ to Ar⁴, L¹, L², R¹ to R⁵, X¹, X²) defined in Formulas (1) and (20) combine.

Evaluation of Manufacture of Organic Electric Element Example 1) Manufacture and Evaluation of Red Organic Light Emitting Diode(Single Host)

First, on an ITO layer(anode) formed on a glass substrate, N¹-(naphthalen-2-yl)-N⁴,N⁴-bis(4-(naphthalen-2-yl(phenyl)amino)phenyl)-Ni-phenyl benzene-1,4-diamine(hereinafter will be abbreviated as 2-TNATA) was vacuum-deposited to form a hole injection layer with a thickness of 60 nm. Subsequently, 4,4-bis [N-(1-naphthyl)-N-phenylamino] biphenyl (hereinafter will be abbreviated as NPB) was vacuum deposited as hole transport compound on the layer to a thickness of 60 nm to form a hole transport layer. The compound represented by Formula (1) was used as a host in the upper of the hole transport layer, and (piq)₂Ir(acac) [bis-(1-phenylisoquinolyl)iridium(III)acetylacetonate] was used as a dopant material, doped at a weight ratio of 95:5, and vacuum deposited at a thickness of 30 nm to form an emitting layer on the hole transport layer. Subsequently, (1,1′-bisphenyl)-4-olato)bis(2-methyl-8-quinolinolato)aluminum (hereinafter will be abbreviated as BAlq) was vacuum deposited to a thickness of 10 nm to form a hole blocking layer, and tris(8-quinolinol)aluminum(hereinafter will be abbreviated as Alq3) was vacuum deposited to a thickness of 40 nm to form an electron transport layer. Thereafter, an alkali metal halide, LiF was deposited to a thickness of 0.2 nm to form an electron injection layer, and Al was deposited to a thickness of 150 nm to use a cathode to manufacture an OLED.

To the OLEDs which were manufactured by examples and comparative examples, a forward bias direct current voltage was applied, and electroluminescent (EL) properties were measured using PR-650 of Photoresearch Co., and T95 life was measured using a life measuring apparatus manufactured by McScience Inc. with a reference luminance of 5000 cd/m². In the following table, the manufacture of a device and the results of evaluation are shown.

Comparative Examples 1 to 7

An organic electroluminescent device was manufactured in the same manner as in Example 1, except that Comparative Compound A, Comparative Compound B, Comparative Compound C, Comparative Compound D, Comparative Compound E, Comparative Compound F and Comparative Compound G were used as the host material.

TABLE 7 Current Brightness Lifetime CIE compound Voltage Density (cd/m²) Efficiency T(95) (x, y) Comparative comparative 7.1 24.5 2500.0 10.2 72.9 (0.66, 0.32) example (1) compound A comparative comparative 6.9 18.6 2500.0 13.4 84.3 (0.65 0.32) example (2) compound B comparative comparative 6.8 18.3 2500.0 13.7 83.3 (0.66, 0.33) example (3) compound C comparative comparative 6.3 17.5 2500.0 14.3 104.8 (0.66, 0.35) example (4) compound D comparative comparative 5.6 13.2 2500.0 19.0 124.8 (0.65 0.32) example (5) compound E comparative comparative 6.9 18.4 2500.0 13.6 82.9 (0.66, 0.35) example (6) compound F comparative comparative 5.4 15.3 2500.0 16.3 122.6 (0.66, 0.35) example (7) compound G example (1) compound (3-1) 4.9 12.5 2500.0 20.0 125.9 (0.66, 0.35) example (2) compound (3-23) 4.9 11.4 2500.0 22.0 125.0 (0.66, 0.35) example (3) compound (3-28) 5.0 11.4 2500.0 21.9 126.0 (0.66, 0.35) example (4) compound (3-32) 4.8 10.5 2500.0 23.9 127.6 (0.66, 0.35) example (5) compound (3-36) 4.9 11.4 2500.0 22.0 127.9 (0.66, 0.35) example (6) compound (3-44) 5.0 10.9 2500.0 23.0 128.2 (0.66, 0.35) example (7) compound (3-51) 5.0 11.7 2500.0 21.4 127.2 (0.66, 0.35) example (8) compound (3-64) 4.9 11.3 2500.0 22.1 129.0 (0.66, 0.35) example (9) compound (3-80) 4.9 12.0 2500.0 20.8 128.5 (0.66, 0.35) example (10) compound (4-4) 4.9 10.0 2500.0 25.1 128.2 (0.66, 0.35) example (11) compound (4-23) 4.7 9.2 2500.0 27.1 129.2 (0.66, 0.35) example (12) compound (4-32) 4.9 9.6 2500.0 26.0 128.9 (0.66, 0.35) example (13) compound (4-49) 4.9 9.5 2500.0 26.2 127.5 (0.66, 0.35) example (14) compound (4-61) 4.9 9.9 2500.0 25.4 125.6 (0.66, 0.35) example (15) compound (4-71) 5.1 9.4 2500.0 26.6 125.9 (0.66, 0.35) example (16) compound (4-86) 4.9 9.5 2500.0 26.2 126.9 (0.66, 0.35)

As can be seen from the results of Table 7, when the material for an organic electroluminescence device of the present invention is used as the phosphorescent host, it was confirmed that the driving voltage and the efficiency were remarkably improved.

That is, The results of Comparative Example F, which is a Bis-Cz compound, were superior to Comparative Compound A, which is CBP generally used as a host material, and Comparative Examples B, C, D and E, which are polycyclic ring compounds, showed better results than Comparative Example F. Among the polycyclic ring compounds B to E, the results of comparative compound D in which the different hetero elements were substituted were superior to those of Comparative Examples B and C in which the same hetero element was substituted, and Comparative compounds E and G, which are herbicidal compounds having one more benzene fused at a specific position in comparative compound D, showed excellent results in driving voltage, efficiency, and lifetime. In addition, it can be seen that the compounds of the present invention, which are 7 ring compounds in which benzene is further fused at a specific position in the comparative compounds E and G cores, show remarkably superior results in all aspects than the comparative compounds E and G. This can be confirmed by looking at the results of HOD and EOD in FIGS. 2 and 3, as one more benzene is fused at a specific location, not only is hole mobility faster, but electron mobility is also faster. That is, depending on whether the hetero-atoms are the same or different, or whether benzene is more fused in 5 or 6 rings or not, chemical properties such as energy level and thermal stability of the core compound are changed, and property of the element such as EOD, HOD, and packing density are change, and as a result, significantly different device characteristics may appear.

Example 2) Manufacture and Evaluation of Red Organic Light Emitting Diode (Mixed Host)

First, on an ITO layer(anode) formed on a glass substrate, N¹-(naphthalen-2-yl)-N⁴,N⁴-bis(4-(naphthalen-2-yl(phenyl)amino)phenyl)-N-phenyl benzene-1,4-diamine(hereinafter will be abbreviated as 2-TNATA) was vacuum-deposited to form a hole injection layer with a thickness of 60 nm, and N,N′-bis(1-naphthalenyl)-N,N′-bis-phenyl-(1,1′-biphenyl)-4,4′-diamine (hereinafter will be abbreviated as NPB) was vacuum-deposited to form a hole transport layer with a thickness of 60 nm. On the hole transport layer, a mixture of the compounds represented by Formulas (1) and (20) as a host in a ratio of 3:7 was used as a host, and as a dopant, an emitting layer with a thickness of 30 nm was deposited on the hole transport layer by doping (piq)₂Ir(acac) [bis-(1-phenylisoquinolyl)iridium(III)acetylacetonate] with a weight of 95:5. (1,1′-bisphenyl)-4-olato)bis(2-methyl-8-quinolinolato)aluminum (hereinafter abbreviated as BAlq) was vacuum deposited as a hole blocking layer to a thickness of 10 nm, and tris(8-quinolinol)aluminum (hereinafter abbreviated as Alq3) was deposited to a thickness of 40 nm as an electron transport layer. After that, an alkali metal halide, LiF was vacuum deposited as an electron injection layer to a thickness of 0.2 nm, and Al was deposited to a thickness of 150 nm to form a cathode to manufacture an OLED.

To the OLEDs which were manufactured by examples and comparative examples, a forward bias direct current voltage was applied, and electroluminescent(EL) properties were measured using PR-650 of Photoresearch Co., and T95 life was measured using a life measuring apparatus manufactured by McScience Inc. with a reference luminance of 2500 cd/m². In the following table, the manufacture of a device and the results of evaluation are shown.

Comparative Example 7

An organic electroluminescent device was manufactured in the same manner as in Example 1, except that Comparative Compound B and Comparative Compound C were mixed and used as a host.

Comparative Example 8

An organic electroluminescent device was manufactured in the same manner as in Example 1, except that Comparative Compound D and Comparative Compound F were mixed and used as a host.

Comparative Example 9

An organic electroluminescent device was manufactured in the same manner as in Example 1, except that Compound 2-5, which is one of the compounds represented by Formula (20), and Comparative Compound F were mixed and used as a host.

TABLE 8 Current Brightness Lifetime First host Second host Voltage Density (cd/m²) Efficiency T(95) comparative comparative comparative 5.9 13.0 2500.0 19.3 103.8 example (7) compound B compound C comparative comparative comparative 5.6 10.5 2500.0 23.9 108.9 example (8) compound D compound F comparative compound (2-5) comparative 5.4 10.0 2500.0 25.0 111.2 example (9) compound F example (17) compound (1-1) compound (3-1) 4.3 8.4 2500.0 29.9 133.9 example (18) compound (1-6) compound (3-1) 4.3 8.4 2500.0 29.9 133.4 example (19) compound (1-9) compound (3-1) 4.4 8.4 2500.0 29.6 133.1 example (20) compound (1-28) compound (3-1) 4.3 8.4 2500.0 29.7 133.7 example (21) compound (1-54) compound (3-1) 4.3 8.3 2500.0 30.0 133.3 example (22) compound (2-5) compound (3-1) 4.5 8.4 2500.0 29.8 133.1 example (23) compound (2-17) compound (3-1) 4.4 8.6 2500.0 29.2 133.8 example (24) compound (2-40) compound (3-1) 4.5 8.5 2500.0 29.5 133.6 example (25) compound (2-41) compound (3-1) 4.5 8.6 2500.0 29.2 134.7 example (26) compound (2-49) compound (3-1) 4.5 8.5 2500.0 29.4 133.7 example (27) compound (1-1) compound (3-23) 4.3 7.8 2500.0 32.2 137.7 example (28) compound (1-6) compound (3-23) 4.4 7.7 2500.0 32.5 135.7 example (29) compound (1-9) compound (3-23) 4.4 8.0 2500.0 31.4 135.8 example (30) compound (1-28) compound (3-23) 4.3 7.9 2500.0 31.7 137.5 example (31) compound (1-54) compound (3-23) 4.5 8.3 2500.0 30.2 135.6 example (32) compound (2-5) compound (3-23) 4.4 7.6 2500.0 32.8 137.1 example (33) compound (2-17) compound (3-23) 4.4 7.7 2500.0 32.3 135.8 example (34) compound (2-40) compound (3-23) 4.3 7.7 2500.0 32.5 135.5 example (35) compound (2-41) compound (3-23) 4.4 8.2 2500.0 30.4 135.8 example (36) compound (2-49) compound (3-23) 4.4 7.9 2500.0 31.6 135.4 example (37) compound (1-1) compound (3-32) 4.4 8.3 2500.0 30.1 135.7 example (38) compound (1-6) compound (3-32) 4.3 7.8 2500.0 32.0 136.5 example (39) compound (1-9) compound (3-32) 4.5 7.8 2500.0 31.9 137.7 example (40) compound (1-28) compound (3-32) 4.4 8.3 2500.0 30.1 136.6 example (41) compound (1-54) compound (3-32) 4.5 8.2 2500.0 30.6 136.3 example (42) compound (2-5) compound (3-32) 4.5 8.3 2500.0 30.2 137.7 example (43) compound (2-17) compound (3-32) 4.4 8.2 2500.0 30.5 137.0 example (44) compound (2-40) compound (3-32) 4.3 7.9 2500.0 31.6 135.8 example (45) compound (2-41) compound (3-32) 4.5 8.2 2500.0 30.6 135.5 example (46) compound (2-49) compound (3-32) 4.4 7.6 2500.0 32.8 136.6 example (47) compound (1-1) compound (4-4) 4.1 8.0 2500.0 31.2 139.6 example (48) compound (1-6) compound (4-4) 4.2 8.1 2500.0 31.0 140.0 example (49) compound (1-9) compound (4-4) 4.1 7.9 2500.0 31.6 138.2 example (50) compound (1-28) compound (4-4) 4.1 8.0 2500.0 31.4 139.6 example (51) compound (1-54) compound (4-4) 4.1 8.1 2500.0 31.0 138.6 example (52) compound (2-5) compound (4-4) 4.1 8.0 2500.0 31.3 138.4 example (53) compound (2-17) compound (4-4) 4.2 7.9 2500.0 31.8 139.9 example (54) compound (2-40) compound (4-4) 4.2 7.9 2500.0 31.6 139.5 example (55) compound (2-41) compound (4-4) 4.2 8.0 2500.0 31.2 138.2 example (56) compound (2-49) compound (4-4) 4.0 7.9 2500.0 31.6 139.8 example (57) compound (1-1) compound (4-23) 3.8 6.5 2500.0 38.6 148.9 example (58) compound (1-6) compound (4-23) 3.9 6.5 2500.0 38.7 147.0 example (59) compound (1-9) compound (4-23) 3.8 6.8 2500.0 36.9 148.1 example (60) compound (1-28) compound (4-23) 3.9 6.6 2500.0 38.1 149.2 example (61) compound (1-54) compound (4-23) 3.8 7.1 2500.0 35.1 147.9 example (62) compound (2-5) compound (4-23) 3.8 6.6 2500.0 37.7 148.3 example (63) compound (2-17) compound (4-23) 3.9 6.3 2500.0 39.4 147.1 example (64) compound (2-40) compound (4-23) 3.8 6.5 2500.0 38.4 146.7 example (65) compound (2-41) compound (4-23) 3.9 7.0 2500.0 35.6 148.8 example (66) compound (2-49) compound (4-23) 3.8 6.5 2500.0 38.6 147.0 example (67) compound (1-1) compound (4-32) 4.2 7.3 2500.0 34.1 143.2 example (68) compound (1-6) compound (4-32) 4.1 7.4 2500.0 33.7 143.0 example (69) compound (1-9) compound (4-32) 4.3 7.5 2500.0 33.3 144.4 example (70) compound (1-28) compound (4-32) 4.3 7.2 2500.0 34.5 142.7 example (71) compound (1-54) compound (4-32) 4.0 7.2 2500.0 34.8 142.0 example (72) compound (2-5) compound (4-32) 4.0 7.2 2500.0 34.6 142.3 example (73) compound (2-17) compound (4-32) 4.0 7.4 2500.0 33.8 143.4 example (74) compound (2-40) compound (4-32) 4.1 7.5 2500.0 33.4 142.9 example (75) compound (2-41) compound (4-32) 4.0 7.6 2500.0 33.0 140.7 example (76) compound (2-49) compound (4-32) 4.1 7.2 2500.0 34.7 144.4 example (77) compound (1-1) compound (4-49) 4.2 7.3 2500.0 34.3 143.0 example (78) compound (1-6) compound (4-49) 4.2 7.1 2500.0 35.0 140.2 example (79) compound (1-9) compound (4-49) 4.3 7.2 2500.0 34.5 142.8 example (80) compound (1-28) compound (4-49) 4.2 7.5 2500.0 33.2 141.6 example (81) compound (1-54) compound (4-49) 4.2 7.5 2500.0 33.3 143.9 example (82) compound (2-5) compound (4-49) 4.0 7.3 2500.0 34.4 141.6 example (83) compound (2-17) compound (4-49) 4.3 7.4 2500.0 34.0 140.3 example (84) compound (2-40) compound (4-49) 4.3 7.2 2500.0 35.0 143.5 example (85) compound (2-41) compound (4-49) 4.1 7.2 2500.0 34.7 143.3 example (86) compound (2-49) compound (4-49) 4.2 7.2 2500.0 34.9 141.1 example (87) compound (1-1) compound (4-61) 4.1 7.2 2500.0 34.5 144.7 example (88) compound (1-6) compound (4-61) 4.2 7.2 2500.0 34.6 144.5 example (89) compound (1-9) compound (4-61) 4.3 7.2 2500.0 34.6 143.4 example (90) compound (1-28) compound (4-61) 4.3 7.6 2500.0 33.1 141.3 example (91) compound (1-54) compound (4-61) 4.2 7.5 2500.0 33.1 141.4 example (92) compound (2-5) compound (4-61) 4.0 7.5 2500.0 33.4 140.3 example (93) compound (2-17) compound (4-61) 4.2 7.3 2500.0 34.3 140.3 example (94) compound (2-40) compound (4-61) 4.1 7.2 2500.0 34.5 142.6 example (95) compound (2-41) compound (4-61) 4.1 7.3 2500.0 34.2 144.3 example (96) compound (2-49) compound (4-61) 4.1 7.4 2500.0 33.7 143.1

As can be seen from the results of Table 8, when the material for an organic electroluminescence device of the present invention represented by Formulas (1) and (20) is mixed and used as a phosphorescent host, it was confirmed that the driving voltage, efficiency, and life span were significantly improved as compared with Comparative Examples 7 to 9 in which the comparative compounds were mixed.

Comparing Comparative Example 7 with Comparative Example 8, it was confirmed that Comparative Example 8 using a mixture containing a polycyclic compound having heteroatoms (N, S) which are different from each other in the 5-ring compound showed a higher efficiency than Comparative Example 7 in which a 5-ring compound having the same nitrogen atom was mixed.

Comparing Comparative Example 9 using a mixture of Compound 2-5 and Comparative Compound F corresponding to Formula (20) and Comparative Example 8 using a mixture of Comparative Compound D and Comparative Compound F in the compound of the present invention, when the comparative compound F is commonly used, and a polycyclic ring compound having a hetero atom (N, S), and a compound 2-5 corresponding to Formula (1) of the present invention were used as a host material, Comparative Example 9 using the compound 2-5 of the present invention shows a higher efficiency and a comparatively higher lifetime.

Examples 17 to 96, which were prepared by mixing the compounds of Formula (1) and the compound of Formula (20) as the host compounds, exhibited significantly higher efficiency and longer lifetime than Comparative Examples 7 to 9

On the basis of the above experimental results, the inventors of the present invention have determined that a substance obtained by mixing the substance of Formula (1) and the substance of Formula (20) has novel characteristics other than those for the respective substances, and measured PL lifetime using the material of Formula (1), the material of Formula (20), and the mixture of the present invention, respectively. As a result, it was confirmed that a new PL wavelength was formed unlike the case of the single compound, when the inventive compound, Formula (1) was mixed with the compound of Formula (20) and that the decrease and decay time of the newly formed PL wavelengths increases from about 60 times to about 360 times less than the decrease and decay times of each of Formula (1) and Formula (20) materials. That is, when the compound of the present invention is mixed and used, it is considered that not only the electrons and holes are moved through the energy level of each material but also the efficiency and lifetime are increased due to the electron, hole transport or energy transfer by the new region(exciplex) having the new energy level formed by the mixing. As a result, when the mixture of the present invention is used, the mixed thin film is an important example showing exciplex energy transfer and light emission processes.

The reason why the combination of the present invention is superior to Comparative Examples 7 to 9 in which a comparative compound is used as a phosphorescent host is that the high T1 and high LUMO energy values improve the electron blocking ability and allow more holes to be moved to the emitting layer more quickly and easily when a compound represented by the general Formula (20) having a strong hole property is mixed with a polycyclic compound represented by Formula (1), which is characterized not only by electron but also by hole stability and high T1. As a result, the charge balance in the emitting layer of holes and electrons is increased, so that light emission is well performed inside the emitting layer rather than at the interface of the hole transport layer, and therefore the deterioration in the HTL interface is also reduced, thereby maximizing the driving voltage, efficiency and life span of the device.

That is, it is considered that the combination of Formula (1) and Formula (20) is electrochemically synergistic to improve the performance of the entire device.

Example 3) Manufacture and Evaluation of Red Organic Light Emitting Diode by Mixing Ratio

TABLE 9 Mixing ratio First Second (first host:second Current Brightness Lifetime host host host) Voltage Density (cd/m²) Efficiency T(95) example compound compound 2:8 4.4 8.0 2500.0 31.2 137.8 (101) (1-54) (3-32) example compound compound 3:7 4.5 8.2 2500.0 30.6 136.3 (102) (1-54) (3-32) example compound compound 4:6 4.7 8.7 2500.0 28.7 120.4 (103) (1-54) (3-32) example compound compound 5:5 4.9 9.2 2500.0 27.1 118.2 (104) (1-54) (3-32) example compound compound 2:8 3.8 6.7 2500.0 37.4 149.0 (105) (2-5) (4-23) example compound compound 3:7 3.8 6.6 2500.0 37.7 148.3 (106) (2-5) (4-23) example compound compound 4:6 4.0 7.1 2500.0 35.1 145.2 (107) (2-5) (4-23) example compound compound 5:5 4.2 7.4 2500.0 33.6 141.8 (108) (2-5) (4-23)

As shown in Table 9, the mixture of the compound of the present invention was measured by fabricating the device in ratio (2:8, 3:7, 4:6, 5:5).

To explain the results in detail, in the result of the mixture of the compound 1-54 and the compound 3-6, the results of the driving voltage, the efficiency and the life span were similarly excellent at 2:8 and 3:7, but as the ratio of the first host increases, such as 4:6 and 5:5, the results of the driving voltage, the efficiency and the life span are gradually decreased, this was also the same in the result of the mixture of the compound 2-5 and the compound 4-23. This can be explained by the fact that the charge balance in the emitting layer is maximized when an appropriate amount of the compound represented by Formula (20) having strong hole properties such as 2:8 and 3:7 is mixed.

Although exemplary embodiments of the present invention have been described for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. Therefore, the embodiment disclosed in the present invention is intended to illustrate the scope of the technical idea of the present invention, and the scope of the present invention is not limited by the embodiment. The scope of the present invention shall be construed on the basis of the accompanying claims, and it shall be construed that all of the technical ideas included within the scope equivalent to the claims belong to the present invention. 

What is claimed is:
 1. A compound represented by Formula (1) below:

wherein, 1) Ar⁴ is selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) where, L′ is selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic, and the R_(a) and R_(b) are independently selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic group containing at least one hetero atom of O, N, S, Si, or P, 2) c is an of 0 to 6, and d and e are integer of 0 to 4, 3) R³, R⁴ and R⁵ are the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)); or in case c, d and e are each an integer of 2 or more, R³, R⁴ and R⁵ are each in plural being the same or different and a plurality of R³s or a plurality of R⁴s or a plurality of R⁵s may combine to each other to form a ring, 4) L² is independently selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic group, 5) X¹ is O or S, wherein the aryl group, fluorenyl group, arylene group, heterocyclic group, fused ring group, alkyl group, alkenyl group, alkoxy group and aryloxy group may be substituted with one or more substituents selected from the group consisting of deuterium; halogen; a silane group substituted or unsubstituted with C₁-C₂₀ alkyl group or C₆-C₂₀ aryl group; siloxane group; boron group; germanium group; cyano group; nitro group; -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined above; a C₁-C₂₀ alkylthio group; C₁-C₂₀ alkoxyl group; C₁-C₂₀ alkyl group; C₂-C₂₀ alkenyl group; C₂-C₂₀ alkynyl group; C₆-C₂₀ aryl group; C₆-C₂₀ aryl group substituted with deuterium; a fluorenyl group; C₂-C₂₀ heterocyclic group; C₃-C₂₀ cycloalkyl group; C₇-C₂₀ arylalkyl group and C₈-C₂₀ arylalkenyl group, and also, these substituents may combine each other and form a ring, wherein the term ‘ring’ means C₃-C₆₀ aliphatic ring or C₆-C₆₀ aromatic ring or a C₂-C₆₀ heterocyclic ring or a fused ring formed by the combination of them, and includes a saturated or unsaturated ring.
 2. The compound according to claim 1, wherein the compound represented by Formula (1) is a compound represented by the following Formula (2):

wherein, 1) R³, R⁴, R⁵, L², c, d, e and X¹ are the same as defined in claim 1, 2) Z¹, Z², and Z³ are each independently selected from the group consisting of CR⁰ or N, and R⁰ is each independently selected from the group consisting of hydrogen; deuterium; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined in claim 1; 3) z is an integer of 0 to 2, 4) R¹¹ being the same or different from each other when z is 2, is independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined in claim 1; or R¹¹ may combine with R⁰ of Z or adjacent R¹¹ when z is 2 to form an aromatic or heteroaromatic ring.
 3. The compound according to claim 2, wherein at least one of Z¹, Z² and Z³ in Formula (2) is N.
 4. The compound according to claim 1, wherein the compound represented by Formula (1) is represented by any of the following Formulas (3) to (7):

wherein, 1) R³, R⁴, R⁵, L², c, d, e and X¹ are the same as defined in claim 1, 2) z is an integer of 0 to 2, 3) R¹ being the same or different from each other when z is 2, is independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined in claim 1; or R¹¹ may combine with R⁰ of Z or adjacent R¹¹ when z is 2 to form an aromatic or heteroaromatic ring.
 5. The compound according to claim 1, wherein the compound represented by Formula (1) is represented by any of the following Formulas (8) to (19);

wherein 1) R³, R⁴, R⁵, L², c, d, e and X are the same as defined in claim 1, 2) Z¹, Z², and Z³ are each independently selected from the group consisting of CR⁰ or N, and R⁰ is each independently selected from the group consisting of hydrogen; deuterium; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined in claim 1; 3) Ar⁵ and Ar⁶ are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined in claim 1, 4) Y¹ and Y² are each independently NR′, O, S or CR′R″, and R′ and R″ are each independently hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₃-C₆₀ heterocyclic group; or a C₁-C₅₀ alkyl group, wherein R′ and R″ may combine with each other to form a ring with a spiro.
 6. The compound according to claim 5, wherein at least one of Z¹, Z² and Z³ in any one of Formulas (8) to (19) is N.
 7. An organic electronic element comprising a first electrode, a second electrode, and an organic material layer formed between the first electrode and the second electrode, wherein the organic material layer comprises an emitting layer, and the emitting layer comprises a first host compound represented by the following Formula (20) and a second host compound represented by the following Formula (1) as a phosphorescent light emitting layer:

wherein 1) Ar¹, Ar², Ar³, and Ar⁴ are each independently selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one hetero atom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) where, L′ is selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic, and the R_(a) and R_(b) are independently selected from the group consisting of a C₆-C₆₀ aryl group; a fluorenyl group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic group containing at least one hetero atom of O, N, S, Si, or P, and Ar² and Ar³ may combine to each other to form a ring, 2) a is an integer of 0 to 4, and b is an integer of 0 to 3, and c is an integer of 0 to 6, and d is an integer of 0 to 4, and e is an integer of 0 to 4; 3) R¹, R², R³, R⁴ and R⁵ being the same or different from each other are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined above; or in case a, b, c, and e are an integer of 2 or more and d is 2, R¹, R², R³, R⁴ and R⁵ are each in plural being the same or different, and a plurality of R¹s or a plurality of R²s or a plurality of R³s or a plurality of R⁴s or a plurality of R⁵s may combine to each other to form a ring; 4) L¹ and L² are independently selected from the group consisting of a single bond; a C₆-C₆₀ arylene group; a fluorenylene group; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; and a C₂-C₆₀ heterocyclic group, 6) X1 is O or S, 7) n is an integer of 1 or 2, and when n is 2 each of the two Ar² and the two Ar³ are the same or different from each other, wherein, the aryl group, fluorenyl group, arylene group, heterocyclic group, fused ring group, alkyl group, alkenyl group, alkoxy group and aryloxy group may be substituted with one or more substituents selected from the group consisting of deuterium; halogen; a silane group substituted or unsubstituted with C₁-C₂₀ alkyl group or C₆-C₂₀ aryl group; siloxane group; boron group; germanium group; cyano group; nitro group; -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined above; a C₁-C₂₀ alkylthio group; C₁-C₂₀ alkoxyl group; C₁-C₂₀ alkyl group; C₂-C₂₀ alkenyl group; C₂-C₂₀ alkynyl group; C₆-C₂₀ aryl group; C₆-C₂₀ aryl group substituted with deuterium; a fluorenyl group; C₂-C₂₀ heterocyclic group; C₃-C₂₀ cycloalkyl group; C₇-C₂₀ arylalkyl group and C₈-C₂₀ arylalkenyl group, and also, these substituents may combine each other and form a ring, wherein the term ‘ring’ means C₃-C₆₀ aliphatic ring or C₆-C₆₀ aromatic ring or a C₂-C₆₀ heterocyclic ring or a fused ring formed by the combination of them, and includes a saturated or unsaturated ring.
 8. The compound according to claim 7, wherein the compound represented by Formula (20) is represented by the following Formula (21) or Formula (22):

wherein R¹, R², L¹, Ar¹, Ar², Ar³, a and b are the same as defined in claim
 7. 9. The compound according to claim 7, wherein L¹ and L² in Formulas (1) and (20) are selected from the group consisting of the following formulas (A-1) to (A-12):

wherein, 1) a′, c′, d′ and e′ are each an integer of 0 to 4; b′ is an integer of 0 to 6; f′ and g′ are each an integer of 0 to 3, and h′ is an integer of 0 to 1, 2) R⁶, R⁷ and R⁸ are the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined in claim 7; or when f′ and g′ are an integer of 2 or more, a plurality of R⁶s or a plurality of R⁷s or a plurality of R⁸s being the same or different from each other, may combine to each other to form an aromatic or a heteroaromatic ring, or two adjacent R⁶ and R⁷, or R⁷ and R⁸ may combine to form an aromatic or heteroaromatic ring, 3) Y is NR′, O, S or CR′R″, and R′ and R″ are each independently hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₃-C₆₀ heterocyclic group; or a C₁-C₅₀ alkyl group, wherein R′ and R″ may combine with each other to form a ring with a spiro, 4) Z⁴, Z⁵ and Z⁶ are independently of each other CR′ or N and at least one is N.
 10. The compound according to claim 9, wherein the compound represented by Formula (20) is represented by any of the following Formulas (23) to (26):

wherein, 1) R¹, R², L¹, Ar¹, Ar², Ar³, a and b are the same as defined in claim 7, and 2) R⁶, R⁷, c′, d′, f′, g′ and Y are the same as defined in claim
 9. 11. The compound according to claim 7, wherein the compound represented by Formula (20) is represented by any of the following Formulas (27) to (38):

wherein R¹, R², L¹, Ar¹, Ar², Ar³, a and b are the same as defined in claim
 7. 12. The compound according to claim 7, wherein the compound represented by Formula (20) is represented by the following Formula (39) or Formula (40):

wherein R¹, R², L, Ar¹, Ar², Ar³, a and b are the same as defined in claim
 7. 13. The organic electronic element according to claim 7, wherein n is 1 in Formula (20).
 14. The organic electronic element according to claim 7, wherein n is 2 in Formula (20).
 15. The organic electronic element according to claim 7, wherein the compound represented by Formula (20) is represented by the following Formula (41):

wherein 1) R¹, R², L, Ar¹, Ar², Ar³, a and b are the same as defined above, 2) f is an integer of 0 to 3, and g is an integer of 0 to 4, 3) R⁹ and R¹⁰ are the same or different from each other, and are each independently selected from the group consisting of deuterium; halogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₂-C₆₀ heterocyclic group including at least one heteroatom of O, N, S, Si or P; a fused ring group of a C₃-C₆₀ aliphatic ring and a C₆-C₆₀ aromatic ring; a C₁-C₅₀ alkyl group; a C₂-C₂₀ alkenyl group; a C₂-C₂₀ alkynyl group; a C₁-C₃₀ alkoxyl group; a C₆-C₃₀ aryloxy group; and -L′-N(R_(a))(R_(b)) wherein L′, R_(a) and R_(b) are the same as defined in claim 7; or in case f and g are an integer of 2 or more, a plurality of R⁹s or a plurality of R¹⁰s being the same or different from each other, or adjacent R⁹ and R¹⁰, may combine to each other to form an aromatic or a heteroaromatic ring, 4) Y is NR′, O, S or CR′R″, 5) R′ and R″ are each independently hydrogen; a C₆-C₆₀ aryl group; a fluorenyl group; a C₃-C₆₀ heterocyclic group; or a C₁-C₅₀ alkyl group, wherein R′ and R″ may combine to each other to form a ring with a spiro.
 16. The compound according to claim 1, wherein the compound represented by Formula (1) is represented by the following Formulas 3-1 to 3-92 and Formulas 4-1 to 4-92:


17. The organic electronic element according to claim 7, wherein the compound represented by Formula (20) is represented by the following Formulas 1-1 to 1-68 and Formulas 2-1 to 2-68


18. The compound according to claim 1, wherein the compound represented by Formula (1) is used as a phosphorescent host.
 19. The compound according to claim 1, wherein the compound represented by Formula (1) is used as a red phosphorescent host.
 20. The organic electronic element of claim 7, further comprising at least one hole transporting band layer between the first electrode and the emitting layer, wherein the hole transporting band layer includes a hole transport layer, an emitting auxiliary layer, or both, and the hole transporting band layer includes a compound represented by Formula (20).
 21. The organic electronic element of claim 7, wherein a ratio of the compound represented by Formula (1) to the compound represented by Formula (20) is 1:9 to 9:1 to be used in the emitting layer.
 22. The organic electronic element of claim 20, wherein a ratio of the compound represented by Formula (1) to the compound represented by Formula (20) is 5:5 to 9:1 to be used in the emitting layer.
 23. A display device comprising the organic electronic element of claim 7; and a control part driving the display device.
 24. A display device according to claim 23, wherein the organic electronic element is an OLED, an organic solar cell, an organic photo conductor (OPC), organic transistor (organic TFT), or an element for monochromic or white illumination. 